1.Commodity:Black Annealed Wire

2.Wire diameter:0.5mm-6.0mm

3.Tensile Strength:30kg-70kg/mm2

4. Elongation Rate:10%-25%

5.Weight/Coil: 0.1kg-800kg/coil

6.Packing: Plastic film and PVC weaving bag outside,Plastic film inside and hessian cloth outside

Production Technology:Black annealed wire material is generally composed of Q195 wire rod drawing model into the black iron wire. Selected raw materials by around 1000 ° after high temperature calcination to keep enough time, and then cooling at appropriate rate. The purpose is to reduce the hardness and improve cutting  

machining; Eliminate the residual stress, stable size, reduce the deformation and crack tendency; Fine grains, adjust, eliminate defects.

Application Fields:Mainly used in construction, mining, chemical, welding, welding net hangers, reprocessing, etc. After annealing the wire become soft, increased flexibility, for building tie wire, binding reinforcement effect is better.