Conforming to: GB /T5293  F4A0-H08A  F5A2-H08MnA

Equivalent to: AWS-A5.17  F6A0-EL12  F7A2-EM12K

DIN BAR 188AC10KM

DESCRIPTION AND APPLICATIONS

Agglomerated acid flux for welding of ordinary carbon manganese, low alloy structure and boiler quality steel in combination with appropriate SAW wire (such as EL8,EM12. EM12K). The flux suitable for high speed welding and provides very good weld bead appearance and excellent slag removal even with narrow groove and fillet welds. The other character of LJ-SJ501 is high resistance to cracking and porosity. Especially it is insensitive to oil, rust, scale and dirt on the surface to be welded. Most being applied to double-side with single pass weld and fillet welds. As the consumption of the flux is very low,it is very economical.

• Flux type: Aluminum-Rutile

• Basicity index: 0.5-0.8

• Grain size:2.0-0.28mm(10-60meshes)

Remark

1.       Before welding, fluxes should be baked for two hours at 300-350℃.

2.       Removal of rust, oil, dirt, water, impurities, etc in welding-areas.