AISI 12L14 Steel Round Bar Sheet Plate, JIS SUM24L, DIN 1.0718
1.0718 Steel Characteristics
1.12L14 steel can be machined with higher cutting speeds and larger depths of cut.
2.Adding free-cutting elements to get great cutting performance.
3.It is extremely easy to cut on a lathe, increasing tool life and productivity by 40%.
4.Cutting and process are very easy. The processing efficiency gets better than general steel.
12L14 Steel Application
12L14 is used to manufacture tools which have requirements of high precision in size, high finish in surface, but low mechanical property, such as gears, shafts, bolts, valves, bushings, pins, fittings, spring seat and machine screw, plastic mold, surgical and dental procedures utensils, certain automobile parts, instruments, etc. Lead free-cutting steel has low contact fatigue, so it is not suitable for parts such as gears and bearings that are subjected to fatigue stress and load.
12L14 Steel Round Bar Sheet Plate Heat Treatment
Annealing
Heat to 890℃ – 920℃ hold until temperature is uniform throughout the section, and cool in furnace.
Carburizing
Pack, salt or gas carburize at 900℃ holding for sufficient time to develop the required case depth and carbon content, followed by a suitable refining/hardening and tempering cycle to optimize case and core properties.
Core Refinea
Slow cool from carburizing temperature and re-heat to 880℃ – 900℃, hold until temperature is uniform throughout the section and quench as required in oil, water.
Case Hardening
Following core refining, re-heat to 760℃ – 790℃, hold until temperature is uniform throughout the section and quench in water. Temper immediately while still hand warm.
Tempering – After Carburising, Core Refining and Case Hardening
Re-heat 12L14 steel to 120℃ – 230℃, hold until temperature is uniform throughout the section, soak for 1 hour per 25 mm of section and cool in still air.NB. Tempering will improve the toughness of the case with only slight reduction in case hardness. It will also reduce it’s susceptibility to grinding cracks.
Normalizing
Heat to 900℃ – 940℃ hold until temperature is uniform throughout the section, soak for 10 – 15 minutes. Cool in still air.
Stress Relieving
Heat to 500℃ – 700℃ hold until temperature is uniform throughout the section, soak for 1 hour per 25mm of the section, and cool in still air.
Notes on Heat Treatment
Heating temperatures, rate of heating, cooling and soaking times will vary due to factors such as work piece size/shape, also furnace type employed, quenching medium and work piece transfer facilities etc. Please consult your heat treater for best results.
Machining
It is a premium free cutting steel grade suitable for all types of high production and repetition machining.
Welding
12L14 steel is not recommended for welding due to its lead content. It is a health hazard.
After almost 20 years of development and growth, Songshun Steel becomes one comprehensive special steel factory, stockist and exporter. The excellent customer group, capital conditions, service attitude and professionalism always push us to get better to service customers.
The great experienced exporting team and professional engineer team as our strong back to make everyone understand what Chinese steel really is.songshunsteel4140434011
Dongguan Songshun Mould Steel Co., Ltd. | |
---|---|
Country/Region: | Guang Dong - China |
Business Nature: | Trading Company |
Phone: | 18269260283 |
Contact: | MiKi Zhuo (director) |
Last Online: | 01 Mar, 2023 |