| Model: | RTV1305 |
|---|---|
| Brand: | - |
| Origin: | Made In China |
| Category: | Chemicals / Rubber Materials |
| Label: | silicone rubber , silicone , silicone for parts |
| Price: |
US $8
/ kg
|
| Min. Order: | 200 kg |
| Last Online:16 May, 2014 |
Descripation:
Electronic potting silicone rubber is generally named astwo-part silicone rubber that vulcanizes at room temperature.Part A is a flow able liquid,part B is the platinum catalyst.
Features:
• UL 94V-0
• Water proof
• Good flowability
• Inflaming retarding
• Moderate thermal conductivity
• Room temperature or heat accelerated cure
Benefits:
• Rapid, versatile cure processing controlled by temperature
• Can be considered for uses requiring added flame resistance
Composition:
• 1 to 1 Mix Ratio
• Polydimethylsiloxane
• platinum curing agent
Applications:
Suitable for general potting material for power supplies, connectors, sensors, industrial controls and transformers.
Parameter:
| Before curing | Item NO. | RTV-1305 | |
| Appearance | black | ||
| Viscosity Mpa.s | part A | 3000 | |
| part B | 3400 | ||
| Density(g/cm3) | part A | 1.35-1.40 | |
| part B | 1.38-1.40 | ||
| Ratio(part A+part B) | 10:1 | ||
| Pot life at 25°Cmins | 60 | ||
| De-molding time at 25°C (H) | 24 | ||
| De-molding time at 50°C (H) | 4-6 | ||
| De-molding time at 100°C (H) | 1-2 | ||
| De-molding time at 150°C (H) | 0.5-1 | ||
| After curing | Hardness Shore A | 30-40 | |
| Elongation break% | 50-60 | ||
| Tear strength(KN/m) | 1.8 | ||
| Tensile Strength(Mpa) | 0.5-1.5 | ||
| Volume resistivity/Ω.cm | ≥1014 | ||
| Break down voltage(kv/mm) | ≥15 | ||
| Specific inductive capacity(50Hz) | 2.7-3.3 | ||
| Dielectric loss factor(50Hz) | ≤0.02 | ||
| Thermal conductivity | ≥0.5 | ||
How to make mold?
1.Mixing
Please weight 1 Part A base and 1 parts of platinum Catalyst in a clean container.Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until part B completely dispersed in the base. Hand or mechanical mixing can be used,but do not for an extended period of time or allow the temperature to exceed 35°C. Mix suitably small quantities to ensure thorough mixing of base and catalyst.
It is strongly recommended that entrapped air be removed in a vacuum chamber,allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum,the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
2.Pouring the mixture and curing
Pour the mixed Part A base silicone and part B platinum catalyst as soon as possible onto the original,avoiding air entrapment.The catalyzed material will cure to a flexible rubber within 24 hours(or faster by different mixing ratio or room temperature).
Storage:
When stored at or below 30°C in the original unopened containers,SILASTIC Base and platinum Catalyst have a usable life of 12 months.from the date of production.After 12 months stock,pls use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again,no influence for other performance.
Packing:
Certificate: