Model: | E308L-16 |
---|---|
Brand: | TEMO |
Origin: | Made In China |
Category: | Metallurgy , Mining & Energy / Metallurgy & Mining / Bars, Rods, Angles, and Stainless Steel Shapes |
Label: | welding wire , welding electrode , welding rod |
Price: |
US $1500
/ Ton
|
Min. Order: | 0.2 Ton |
Last Online:26 Jul, 2014 |
Item NO. | GB/TB | AWS | ||||||
WEA002 | E308L-16 | E308L-16 | ||||||
Description:
Type of Cr19Ni10Mo ultra-low carbon stainless steel with coating of titanium calcium electrode.The carbon content in deposited metal less than or equal to 0.04% with good intergranular corrosion satisfying.Both AC/DC connection applicable with excellent welding performance. |
||||||||
Application:
WEA002 Stainless Steel Electrode apply to welding of stainless-steel of low carbon(Cr19Ni10).Can also be used to weld of corrosion resistance stainless steel under the operation temperature lower than 300℃.It is mainly used in synthetic fiber, fertilizer, petroleum equipment. |
||||||||
Chemical composition of Deposited metal(%): | ||||||||
C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
≤0.04 | 0.5-2.5 | ≤0.90 | 18.0-21.0 | 9.0-11.0 | ≤0.75 | ≤0.75 | ≤0.030 | ≤0.040 |
Mechanical Performance of deposited Metal: | ||||||||
Rm(Mpa) | A(%) | |||||||
≥520 | ≥35 | |||||||
※The deposited metal corrosion resistance test and titanium content determined by supply and demand both sides negotiation. | ||||||||
Reference Current:(DC﹢or AC) | ||||||||
Diameter (mm) | Φ2.0 | Φ2.5 | Φ3.2 | Φ4.0 | ||||
Current (A) | 25-50 | 50-80 | 80-110 | 110-160 | ||||
Notes:(Ⅰ)Please bake WEA002 Stainless Steel Electrode for 1 hour at 150℃ before welding .(Ⅱ)We s est you to do the welding by DC and control the current to avoid redenning problem of rodes. By AC, the depth will not be enough. |
right:.��slPM�cy border-left:none;width:108pt'>Φ4.0 Φ5.0 Current (A) 60-90 90-120 140-180 170-230 Notes:(Ⅰ)Please bake WE557 Low Alloy Steel Electrode for 1 hour at about 380℃ before welding .(Ⅱ)Clean the surface to be welded thoroughly to remove surface contaminations.(Ⅲ)Short arc must be used when welding and the weld joint shoulds not be too wide.