AL-Zn METALLIZED POLYESTER & POLYPROPYLENE FILM (ZTM, ZPM), ,CAPACITOR GRADE METALLIZED BOPP FILM 4micro,4.5micro,5micro,6micro,7micro,8micro,9micro,10micro,11 micro,12micro
This film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor, AC capacitor and so on
This film is manufactured with high purity, high isotacticity polypropylene. It has high BDV, excellent mechanical strength.
Product Description
1.Type:Al/Zn Metallized film
Al Metallized film
Safety Anti-explosion Film
2.Application:Applied to capacitors for power system, refrigerators and air conditioners
Construction
3.Aluminum/Zinc film with reinforced edge
4.Specification
Thickness |
µm |
3.3 ~ 6.8 |
3.5 ~ 15 |
- |
Density |
G/cm3 |
1.4 |
0.91±0.01 |
ASTM D 1505/DIN 53 479 |
Tensile Strength |
MD(N/mm2) |
255~274 |
130 |
ASTM D 882/ DIN 53 455 |
|
TD(N/mm2) |
294 |
250 |
ASTM D 882/DIN 53 455 |
Elongation at Break |
MD(%) |
110 |
180 |
ASTM D 882/DIN 53 455 |
|
TD(%) |
100 |
40~70 |
ASTM D 882/DIN 53 455 |
Heat Shrinkage |
MD(%) |
2.2(150oC , 30 min) |
6 ( 6.0 µm ) 5 ( > 6.0 µm ) ( 120°C , 15 min ) |
DIN 40 634 |
|
TD(%) |
0.8~1.0 |
</=1.0 |
DIN 40 634 |
Break-down voltage(BDV) |
V/µm |
1900 |
700( 23oC, DC ) |
DIN 53 481 |
Surface Roughness |
Ra(µm ) |
0.08~ 0.1 |
0.8 |
JIS B 0601/DIN 4762 |
|
Rmax(µm) |
1.39 |
1.09 |
JIS B 0601/DIN 4762 |
Dissipation Factor(20oC, 1KHz) |
10 -4 |
50 |
3 |
DIN 53 483(20oC, 1KHz) |
Dielectric Constant |
- |
3.2 |
2.2±0.1 |
DIN 53 483(20oC, 1KHz) |
Insulation Resistance |
MΩ.μF(20oC) |
30,000 |
100,000 |
DIN 53 482 |
Water Absorption |
% |
0.34 |
<0.1 |
JIS C2318/DIN 53 472 |
Number of Pinhole(Insulation Failure) |
Ea/m2 |
2 |
5 ( 6.5µm ) 2 ( 7µmMMV 11µm ) 1 ( >11µm ) |
- |
Storge
Metallized film should be stored in its original package until its use with temperature 5 ~ 35°C and humidity less than 85%RH.
Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.
The recommended temperature is 15 -25°C with humidity less than 60%RH after the package is open.
With original sealed package, and stored in the above mentioned conditions, the storage time can be as following:
Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period depends on the resistance of the film:
Less than 10 Ohms: 6 months (from delivery date)
10 Ohms to 15 Ohms: 3 months (from delivery date)
15 Ohms: 1months (from delivery date)