Product Description
| Product Introduction |
HDPE has excellent temperature adaptability, good weldability and aging resistance, chemical corrosion resistance, environmental stress cracking resistance and puncture resistance.Therefore, it is especially suitable for the underground engineerings, landfills, sewages or waste residue treatment, mining engineerings as seepage prevention material.
Textured HDPE geomembrane is a new seepage control material,which include single textured, double textured HDPE geomembrane, can increase the friction coefficient, anti-skid function, more conducive to the steep slope and vertical seepage control to improve the engineering stability.
Products series: single textured geomembrane, double-wall textured geomembrane. |
| |
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
| Product Specification |
|
*Thickness: 0.30mm~3.00mm
*Width: 4m~8m.
*Roll length:
PS: Customized request accept for all above.
Geomembrane Series
Textured HDPE Geomembrane For Landfill (CJ-T234-2006) |
|
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
Remark |
| Item |
| Thickness (mm) |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
|
| Textured Highth (mm) |
0.25 |
|
| Density (g/c㎡,≥) |
0.94 |
|
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) |
15 |
18 |
22 |
29 |
37 |
44 |
|
| Breaking Strength (N/mm,LD/TD) |
10 |
13 |
16 |
21 |
26 |
32 |
|
| Yeild Elongation Rate (%) |
12 |
|
| Breaking Elongation Rate (%) |
100 |
|
| Rectangular Tear Strength (N) |
125 |
156 |
187 |
249 |
311 |
374 |
|
| Puncture Strength (N) |
267 |
333 |
400 |
534 |
667 |
800 |
|
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) |
300 |
|
| Carbon Black |
| Carbon Black Content(Rang) (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 |
|
| Oxidative Induction Time (OIT) |
| Standard OIT (min) |
100 |
|
| High Pressure OIT (min) |
400 |
|
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) |
55 |
|
| 90 days after baking, the hight pressure OIT retention(%) |
80 |
|
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) |
50 |
|
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) |
50 |
|
| -70℃ The Low Temperature Embrittlement Performance mpact |
Pass |
|
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) |
≤1.0X10-13 |
|
| Dimensional Stability |
±2 |
|
|
| Payment Terms: | TT / LC / DP / DA |
| |
Product Image
Img 1
Img 2
Img 3
Img 4
Img 5
Send Inquiry to this Member
Related Products of this Company
This member assumes full responsibility for the content of this listing. DIYTrade accepts no responsibility whatsoever in respect of such content.
To report fraudulent or illegal content, please
click here.
China Suppliers Quick Searching:
,