| Model: | D3060 |
|---|---|
| Brand: | DENSO |
| Origin: | Made In China |
| Category: | Chemicals / Coatings, Varnish & Painting |
| Label: | automotive primer , 2k primer , two-component primer |
| Price: |
US $1
/ pc
|
| Min. Order: | 500 pc |
| Last Online:18 Apr, 2015 |
| 2K middle primer D3060 | ||||||||
| Characteristic:two pack middle primer with strong chemical corrosion resisting ability and adhesion,and also have good leveling and gloss performance | ||||||||
| Surstrates | Steel、glass steel and hardened original paint surstrates | |||||||
| Surstrates Treatment | Remove sanded contaminations with degreaser | |||||||
| Mixing Ratio | Temperature |
Name | 2K middle primer D3060 | D-3160 Primer Hardener | 2K Series ThinnerD-310 | |||
According to choose mixing thinner to apply to temperature |
Weight Ratio | 100 Parts | 25Parts | 25Parts | ||||
| Volume Ratio | 10 Parts | 1 Part | 1 Part | |||||
| Pot Life | 4hours,at 250C | |||||||
| Spray viscosity | 20-22 Seconds at /200C | |||||||
| No.of Coats | 2-3coats | |||||||
| Flash-off Time | 5-10 Minutes at 250C | |||||||
| Each thickness | 25-30 Micron | |||||||
Spray Pressure |
Gravity Feed: 1.8/3-4.5kg
Siphon Feed: 1.8/3.5-5kg |
|||||||
| Drying Time | Temperature | Dust Free | Dry to Handle | Thorough Dry | ||||
| 250C | 15 Minutes | 30minutes | 4 Hours | |||||
| 600C | 5 Minutes | 10 Minutes | 30 Minutes | |||||
| Sandability and Polishabiility | Wet sanding with P400-P600, or dry sanding with P320-P400 | |||||||
| Shelf Life | 2K D-3060 middle primer:2 years in original sealed,D3160 primer hardener:1 years in original sealed (can continue to use after passing inspection ) | |||||||
| Packaging | 2K D-3060 middle primer: D3160 hardener:400g | |||||||
| The above products are designed for special using, please reference to the label and detailed security parameter , the product users should comply with the health and safe treatment regulations | ||||||||
| The above technical data is correct, but we don't provides guarantee, because the final result will be effected by the environment and the use of methods. | ||||||||