Model: | NV702 |
---|---|
Brand: | NOVAESTONE |
Origin: | Made In China |
Category: | Construction & Decoration / Slate, Marble, Granite & Stone / Countertop & Vanity Top |
Label: | Quartz Stone , quartz slab , artificial quartz |
Price: |
¥78
/ pc
|
Min. Order: | 400 pc |
Last Online:26 Jun, 2015 |
NOVAESTONE QUARTZ TECHNICAL SPECIFICATIONS
NO. |
TEST ITEM(S) |
TEST METHOD(S) |
TEST RESULT(S) |
1 |
Absorption by Weight |
ASTM C97/C97M - 09 |
0.02% |
2 |
Apparent Density |
2350 kg/m3 |
|
3 |
Abrasion Resistance (Polished) |
ASTM C241/C241M - 13 |
51 |
4 |
Flexural Strength |
ASTM C880/C880M - 09 |
Dry condition: 35.8 MPa |
Wet condition: 38.0 MPa |
|||
5 |
Compression Strength |
ASTM C170/C170M - 09 |
Dry condition: 199 MPa |
Wet condition: 192 MPa |
|||
6 |
Specular Gloss (60o) |
ASTM D523 - 08 |
42.5 |
7 |
Linear Shrinkage and Coefficient of Thermal Expansion |
ASTM C531 - 00 |
36x10-6/°C |
8 |
Mohs' Hardness (Polished) |
EN 101:1991 |
7~8 |
9 |
Linear Thermal Expansion Coefficient |
Refer to ISO 10545-8: 1994 |
35x10-6/°C |
10 |
Abrasion Resistance of Unglazed Tiles (Polished) |
Refer to ISO 10545-6: 2010 |
39 mm3 |
11 |
Radioactivity |
GB 6566 - 2010 |
Class A |
12 |
Load Test |
ANSI Z124.6 - 2007 |
No damage, Average residual deflection: -0.01mm |
13 |
Stain Resistance Test (Polished) |
Total stain resistance value: 37 Maximum individual depth of staining: 0.02mm |
|
14 |
Chemical Resistance Test (Polished) |
Unaffected |
|
15 |
Cigarette Test (Polished) |
Ater test, there were visible stains remains which can be restorable by clean sponge and water |
|
16 |
Heated Pan Test (Polished) |
No visible change after test |
Artificial Quartz Stone as table top
NOVAESTONE
provides this colour in the following slab sizes:
Standard |
3000×1400mm / 120×56'' |
Jumbo |
3200×1600mm / 128×63'' |
Slab thickness |
12mm / 15mm / 20mm / 30mm |
Your specific size measurement may also be accomplished.
We now also offering custom Colour-Matching and Pre-Fabrication service for project works; just bring us your own sample and drawing.