Introduction:
304 Stainless Steel Flat Bar, is for all applications where greater strength and superior corrosion resistance is required. 304 Stainless Steel Flat Bar has a durable dull, grainy mill finish and is widely used for all types of fabrication projects that are exposed to the elements.
Applications:
Frame work, braces, supports, plates, marine, food, etc.
Size Range:
3mm*10mm-30mm*180mm.
All Grades Comparison:
ASTM A304
JIS:SUS304
GB/T 06Cr19Ni10
Chemical Composition(%)
304 C:0.08max, Si:1.00max, Mn:2.0max, P:0.045max, S:0.030max, Cr:18.0-20.0, Ni:8.0-11.0
304L C:0.03max, Si:1.00max, Mn:2.0max, P:0.045max, S:0.030max, Cr:18.0-20.0, Ni:8.0-12.0
304N C:0.08max, Si:1.00max, Mn:2.0max, P:0.045max, S:0.030max, Cr:18.0-20.0, Ni:8.0-11.0, N:0.10-0.16
Mechanical Properties
Steel Grade:304
Delivery Condition:Annealed
Thickness:12.7mm max
Tensile Strength (Mpa):620 Mpa min
Yield Strength (Mpa):310 Mpa min
Elongation in 2 in. (50 mm):30% min
Reduction of Area:40% min
Steel Grade:304
Delivery Condition:Annealed
Thickness:12.7mm min
Tensile Strength (Mpa):515Mpa min
Yield Strength (Mpa):205 Mpa min
Elongation in 2 in. (50 mm):30% min
Reduction of Area:40% min
Steel Grade:304L
Delivery Condition:Annealed
Thickness:12.7mm max
Tensile Strength (Mpa):620 Mpa min
Yield Strength (Mpa):310 Mpa min
Elongation in 2 in. (50 mm):30% min
Reduction of Area:40% min
Steel Grade:304L
Delivery Condition:Annealed
Thickness:12.7mm min
Tensile Strength (Mpa):485 Mpa min
Yield Strength (Mpa):170 Mpa min
Elongation in 2 in. (50 mm):30% min
Reduction of Area:40% min
Steel Grade:304N
Delivery Condition:Annealed
Thickness:Whole Sizes
Tensile Strength (Mpa):550 Mpa min
Yield Strength (Mpa):240 Mpa min
Elongation in 2 in. (50 mm):30% min
Steel Grade:304/304L/304N
Delivery Condition:Relatively severe cold work
Thickness:19.5mm max
Tensile Strength (Mpa):860 Mpa min
Yield Strength (Mpa):690 Mpa min
Elongation in 2 in. (50 mm):12% min
Reduction of Area:35% min
Steel Grade:304/304L/304N
Delivery Condition:Relatively severe cold work
Thickness:19.5-25.4mm
Tensile Strength (Mpa):795Mpa min
Yield Strength (Mpa):550 Mpa min
Elongation in 2 in. (50 mm):15% min
Reduction of Area:35% min
Steel Grade:304/304L/304N
Delivery Condition:Relatively severe cold work
Thickness:25.4-31.75mm
Tensile Strength (Mpa):690Mpa min
Yield Strength (Mpa):345Mpa min
Elongation in 2 in. (50 mm):24% min
Reduction of Area:45% min
Steel Grade:304/304L/304N
Delivery Condition:Strain Hardened
Thickness:50.8mm
Tensile Strength (Mpa):650Mpa min
Yield Strength (Mpa):515Mpa min
Elongation in 2 in. (50 mm):25% min
Reduction of Area:40% min
Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.