17-4PH alloy is a precipitation of copper, niobium / columbium constituted hardening martensitic stainless steel. This level has high strength, degree (up to 300º C / 572º F) and anti-corrosion properties. After heat treatment, the mechanical properties of the product more perfect, can reach up to 1100-1300 mpa (160-190 ksi) of compressive strength. This level can not be used above 300º C (572º F) or under very low temperatures, its atmosphere and dilute acid or salt has good corrosion resistance, corrosion resistance and its 304 and 430 the same.

17-4 Precipitation Hardening also known as Type 630 is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and a moderate level of corrosion resistance. High strength is maintained to approximately 600 degrees Fahrenheit (316 degrees Celsius).

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance.

Mechanical properties can be optimized with heat treatment. Very high yield strength up to 1100-1300 MPa (160-190 ksi) can be achieved.

The grade should not be used at temperatures above 572°F (300°C) or at very low temperatures. It has adequate resistance to atmospheric corrosion or in diluted acids or salts where its corrosion resistance is equivalent to Alloy 304 or 430.

Chemical:

GB....................0Cr17Ni4Cu4NbProcessing

Hot forming

Hot forming should be treated in a certain temperature range, such as 950-1200ºC (1742-2192ºF).

The whole heat treatment includes solid annealing, cooling( lower than 25ºC) and curing.

Cutting

1. Thermal cutting (plasma, sawing, etc.)

Considering the thermal metamorphism, the cutting process should be appropriate. After cutting, it needs to be grinded in order to remove the oxide layer.

2. Mechanical cutting: shear, punching, cold saw, etc.

Machining:

Thermoforming

Hot forming should be carried out within a temperature range 950-1200ºC (1742-2192ºF). Complete heat treatment including solution annealing, cooling (less than 25ºC) and aging (at a given temperature)

Processing

Hot forming

Hot forming should be treated in a certain temperature range, such as 950-1200ºC (1742-2192ºF).The whole heat treatment includes solid annealing, cooling( lower than 25ºC) and curing.

Machining:

ThermoformingHot forming should be carried out within a temperature range 950-1200ºC (1742-2192ºF). Complete heat treatment including solution annealing, cooling (less than 25ºC) and aging (at a given temperature).

welding:17-4 PH alloy can be welded the following:. SMAW, GTAW, PAW and GMAW preliminary test (to check for cracks and weld metal toughness), the SAW welding can be carried out. Because ferrite solidification, reduces the likelihood of weld metal hot cracking and thermal deterioration. In general, does not require preheating, intermediate temperature should be controlled at 120 ° C (248 ° F). After full heat treatment (solution annealing + hardened), the toughness will increase. Martensitic structure due to its own characteristics, the weld metal oxygen content is low to keep the good toughness and ductility. In order to avoid cold cracking, hydrogen intervention should be avoided. 17-4 PH alloy can be filled with the same type of metal (e.g., E 630 (AWS A5.4)? ER 630 (AWS A5.9) welding. If welding without taking into account the mechanical properties of 17-4PH to be austenitic filler metal, then there is no need for heat treatment.

Applications:

• offshore platforms, helicopter deck, other platforms

• Food Industry

• Pulp and paper industry

• Aerospace (turbine blades)

• Mechanical parts

• Nuclear waste barrel