Typical Property |
Item |
TestMethod |
units |
Test value |
||
|
Mechanical properties |
Tensile Strength（Longitudinal） |
ASTM D638 |
Kgf/c ㎡ |
260 |
||
|
/Tensile Strength（Transverse） |
ASTM D638 |
Kgf/c ㎡ |
230 |
|||
|
Impact strength |
ASTM D256 |
Kgf/cm |
7.0 |
|||
|
Tear strength |
ASTM D1922 |
g/mil |
50 |
|||
|
Elongation Ultimate |
ASTM D882 |
% |
200 |
|||
|
TensileModulus |
ASTM D790 |
Mpa |
2300 |
|||
|
Physical Properties |
Density |
|
g/cm3 |
0.92 |
||
|
Hardness |
ISO-868 |
- |
65 |
|||
|
Water absorptionrate |
ASTM D570 |
﹪ |
0. 10 |
|||
|
VEKA softening point |
ASTM D1525 |
℃ |
150 |
|||
|
Electrcal Properties |
Surface Resistivity |
ASTM D257 |
Ω |
1015 |
||
|
Volume Resistance23℃ 50﹪ RH |
ASTM D257 |
Ω-cm |
7 ×1015 |
|||
|
Dielectric Strength |
Thick ness (mm） |
0.125 |
ASTM 149 |
KV/mm |
80 |
|
|
0.175 |
74 |
|||||
|
0.250 |
64 |
|||||
|
0.38 |
60 |
|||||
|
0.430 |
58 |
|||||
|
0.50 |
50 |
|||||
|
0.760 |
40 |
|||||
|
1.000 |
30 |
|||||
|
Thermal Conductivity |
ASTM C177 |
W/m ℃ |
0.18-0.2 |
|||
|
Brittle Temperature |
ASTM D746 |
℃ |
-30 |
|||
|
Surface Dyne Value |
Internal test |
0.125-1.000mm |
38-44 |
|||
|
|
UL 94 |
0.125-0.25mm |
VTM-0 |
|||
|
0.3-1.0mm |
V-0 |
|||||