| Model: | BOPP |
|---|---|
| Brand: | ANHUI SAFE |
| Origin: | Made In China |
| Category: | Electronics & Electricity / Electronic Components / Other Electronic Components |
| Label: | metallized film , film , BOPP film |
| Price: |
US $6
/ Kilogram
|
| Min. Order: | 1 Kilogram |
| Last Online:27 Mar, 2018 |
Different kinds of films to meet your requirements:
1.Aluminum metalized polypropylene film.
2.Aluminum-Zinc alloy metalized polypropylene film.
3.Aluminum-Zinc alloy metalized polypropylene film with heavy edge.
4.Aluminum metalized polyester film.
5.Aluminum-Zinc alloy metalized polyester film.
6.Aluminum-Zinc alloy metalized polyester film with heavy edge.
MPP film:
|
Properties |
Unit |
Requirements |
|
|
Density |
g/cm³ |
0.905±0.005 |
|
|
Thickness |
μm |
3.8~15 |
|
|
Tensile strength |
MD(MPa) |
≥100 |
|
|
Elongation at break |
MD(%) |
40~200 |
|
|
Heat shrinkage |
MD(%) |
≤5(120℃,10min) |
|
|
Break-down voltage |
V/μm |
≥350(23℃，DC) |
|
|
Coating square resistance |
Ω/□ |
with heavy-edge |
heavy-edge area: 3±1 non heavy-edge area: 7.5±2.5 |
|
without heavy-edge |
2~4 |
||
|
Dissipation factor |
— |
≤4x10^(-4) |
|
|
RC |
ΩF |
≥5x10^4 |
|
MPET film:
|
Properties |
Unit |
Requirements |
|||||
|
Density |
g/cm³ |
1.34 |
|||||
|
Thickness |
μm |
＜5 |
5~12 |
＞12 |
|||
|
Tensile strength |
MD(MPa) |
≥84 |
≥108 |
≥120 |
|||
|
Elongation at break |
MD(%) |
≥22 |
≥33 |
≥44 |
|||
|
Break-down voltage |
V/μm |
≥200(23℃, DC) |
≥250(23℃,DC) |
||||
|
Heat shrinkage |
MD(%) |
≤3(120℃, 10min) |
|||||
|
Coating square resistance |
Ω/□ |
Al |
1.5±0.5 |
2.0±0.5 |
2.5±0.5 |
3±1 |
|
|
Zn/Al |
(6~7.5)±30% |
||||||
|
Dissipation factor |
— |
≤60x10^(-4) |
|||||
|
RC |
ΩF |
≥1x10^4 |
|||||
Packing:
1.Roll films are packed in vacuum plastic bags and heat-sealed with desiccants;
2.Bags are marked with labels of types;
3.The bags are packed in cartons;
4.The cartons are wrapped in wooden cases or reinforced carton.
Storage:
1.Metalized film should be stored in its orginal package before using with temperature 5~35℃ and humidity less than 85%RH.
2.Metalized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible once opened.
3.The recommended temperature is 15~25℃ with humidity less than 60%RH once the package is open.
4.With original sealed package and stored as conditions mentioned above, the storage time can be as following:
Alminium metalized film: 12 months from the delivery date;
Zinc-Alminium alloy metalized film: Because Zinc is relatively unstable, preservation period(from delivery date)
depends on the resistance of the film:
≤10Ω/□: 6months
10~15Ω/□: 3months
＞15Ω/□: 1months.
Contact us
Add:No.1771, QiFeng Road, Shizishan Economic Development Zone, Tongling, Anhui, China(mainland)
Tel:0086-562-2821018
Fax:0086-562-2821558
Contact: Helen Hu
Mobile/Whatsapp/Wechat : +86 133 0562 0368
Email: ahsfhzh@hotmail.com
Website: www.film-capacitor.com