GH4080A |
NCF 80A |
Nimonic 80A |
N07080 |
NiCr20TiAl |
2.4952 |
NiCr20TiAl NC20TA |
NiCr20TiAl N80A |
*Product Forms
Pipe, Tube, Sheet, Strip, Plate, Round Bar, Flat Bar, Forgings, Hexagon, Wire
*Brief
Alloy 80A (Nimonic alloy 80A) is a wrought, age-hardenable nickel-chromium alloy. Alloy 80A is similar to alloy 75 but made precipitation hardenable by additions of aluminium and titanium. Alloy 80A has good corrosion and oxidation resistance and high tensile and creep-rupture properties at temperatures to 815℃ (1500ºF). Vacuum refined versions are also available. Alloy 80A is used for gas-turbine components (blades, rings, discs), bolts, tube supports in nuclear generators, exhaust valves in internal combustion engines and has many other offshore/marine, automotive and electrical applications.
*Chemical Composition,%
|
% |
Ni |
Cr |
Fe |
C |
Mn |
Si |
P |
S |
Cu |
Co |
Ti |
Al |
|
Min |
Rest |
18.0 |
|
|
|
|
|
|
|
|
1.80 |
1.00 |
|
Max |
21.0 |
3.00 |
0.10 |
1.00 |
1.00 |
0.02 |
0.015 |
0.20 |
2.00 |
2.70 |
1.80 |
*Typical Physical & Mechanical Property(Solution Annealed)
|
Density |
Melting point |
Tensile strength, MPa |
Yield strength, MPa |
Elongation,% |
|
8.19 g/cm3 |
1320-1365℃ |
980 |
650 |
20 |
*Specification
|
Rod, Bar, Wire, Forgings |
BS 3076&HR 1, ASTM B637 |
|
Plate, Sheet, Strip |
BS HR 201 |
|
Pipe, Tube |
BS HR 401 |
|
Others |
ASTM B366/ASME SB366(Fittings), DIN 17742 |
*Feature
A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile and creep-rupture properties at temperatures to 1500°F (815°C).
*Application
Used for gasturbine components (blades, rings, and discs), bolts, tube supports in nuclear steam generators, die-casting inserts and cores, and exhaust valves in internal-combustion engines.