-------------------------------------------------Technical Information-------------------------------------------------------
ENGAGE™ 8137
Polyolefin Elastomer
® ™ Trademark of The Dow Chemical Company (“Dow”) or an affiliated company of Dow.
Overview
ENGAGE™ 8137 Polyolefin Elastomer is an ethylene-octene copolymer with low density and a high melt index. This
combination provides excellent toughness, flexibility, and ease in processing and makes ENGAGE 8137 highly
effective as an impact modifier in polyolefins or as a component in injection molding applications.
Main Characteristics:
• Pellet form
• Low density
• Excellent flow characteristics
• Toughness, flexibility
• Talc dusted (untreated, 1 μm)
Applications:
• Injection molded industrial and consumer durable goods
• Impact modification
Physical Nominal Value (English) Nominal Value (SI) Test Method
Density 0.864 g/cm³ 0.864 g/cm³ ASTM D792
Melt Index (190°C/2.16 kg) 13 g/10 min 13 g/10 min ASTM D1238
Mooney Viscosity (ML 1+4, 250°F (121°C)) 4 MU 4 MU ASTM D1646
Mechanical Nominal Value (English) Nominal Value (SI) Test Method
Tensile Modulus - 100% Secant
1 (Compression Molded)
261 psi 1.80 MPa ASTM D638
Tensile
Strength 1 (Break, Compression Molded)
348 psi 2.40 MPa ASTM D638
Tensile Elongation 1 ASTM D638
Break, Compression Molded 800 % 800 %
Flexural Modulus ASTM D790
1% Secant : Compression Molded 1130 psi 7.80 MPa
2% Secant : Compression Molded 1060 psi 7.30 MPa
Elastomers Nominal Value (English) Nominal Value (SI) Test Method
Tear Strength 2 151 lbf/in 26.4 kN/m ASTM D624
Hardness Nominal Value (English) Nominal Value (SI) Test Method
Durometer Hardness ASTM D2240
Shore A, 1 sec, Compression Molded 63 63
Shore D, 1 sec, Compression Molded 13 13
Thermal Nominal Value (English) Nominal Value (SI) Test Method
Glass Transition Temperature -67.0 °F -55.0 °C Dow Method
Melting Temperature (DSC) 3 133 °F 56.0 °C Dow Method
Peak Crystallization Temperature (DSC) 100 °F 38.0 °C Dow Method
Additional Information
Properties measured on product without talc dusting.
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm results by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min