Reactive Acrylic Adhesive
The two-part acrylic adhesive, whose curing properties do not change much even if the mixing ratio and mixing status vary, has user friendliness almost equal to that of one-part adhesive.
Features
Application
Product details
・Multi-purpose type : Y600, Y600H, Y610, Y620
・High heat resistance type : Y611BLACK S, Y612BLACK
・Flexible type : Y618LD, Y618H, Y630D
・Conventional type (*Odorous) : Y650
Product data
Adhesive strength by mixing ratio
Oil surface adhesion
Heat aging resistance
High temperature high humidity durability
Heat shock testing
Chemical resistance
Property
Multi-purpose type
| Y600 | Y600H | Y610 | Y620 | |||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Agent A | Agent B | Agent A | Agent B | Agent A | Agent B | Agent A | Agent B | |||
| Application / Properties / Features | High speed curing | High viscosity | High strength | Slow curing | ||||||
| Base | Acrylic resin | Acrylic resin | Acrylic resin | Acrylic resin | ||||||
| External appearance | Light blue | Blue | White | Gray | White | Gray | Light yellow | Blue | ||
| Viscosity | mPa･s/23°C | 4,000 | 4,000 | 30,000 | 30,000 | 5,500 | 5,500 | 8,000 | 8,000 | |
| Mixing ratio | 1:1 | 1:1 | 1:1 | 1:1 | ||||||
| Pot life *1 | 23°C | 30 s | 2 min | 3 min | 6 min | |||||
| Set time *2 | 23°C | 3 min | 4 min | 6 min | 20 min | |||||
| Adhesive property | Tensile shear strength | MPa | 23.2 | 19.4 | 26.0 | 21.1 | ||||
| T-peel strength | N/mm | 5.0 | 3.6 | 3.7 | 4.2 | |||||
| Curing properties | Hardness | Shore A | 68 | 65 | 72 | 66 | ||||
| Glass transfer point | °C | 83 | 78 | 90 | 79 | |||||
| Elastic modulus | MPa | 767 | 742 | 935 | 778 | |||||
| Breaking strength | MPa | 16.2 | 14.0 | 19.0 | 16.1 | |||||
| Elongation at break | % | 26 | 8 | 6 | 25 | |||||
| Capacity | 600g set | 50g set | 50g set | 600g set | ||||||
| 10kg | 600g set | 2kg | ||||||||
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
High heat resistance type
| Y611BLACK S | Y612BLACK | |||||
|---|---|---|---|---|---|---|
| Agent A | Agent B | Agent A | Agent B | |||
| Application / Properties / Features | Hight strength / High heat resistance | |||||
| Base | Acrylic resin | Acrylic resin | ||||
| External appearance | Light yellow | Black | Light yellow | Black | ||
| Viscosity | Pa･s/23°C | 3,000 | 3,000 | 15,000 | 15,000 | |
| Mixing ratio | 1:1 | 1:1 | ||||
| Pot life *1 | 23°C | 3 min | 1 min | |||
| Set time *2 | 23°C | 7 min | 3 min | |||
| Adhesive property | Tensile shear strength | MPa | 28.4 | 29.2 | ||
| T-peel strength | N/mm | 4.2 | 4.3 | |||
| Curing properties | Hardness | Shore D | 84 | 86 | ||
| Glass transfer point | °C | 123 | 127 | |||
| Elastic modulus | MPa | 1558 | 1615 | |||
| Breaking strength | MPa | 32.9 | 33.7 | |||
| Elongation at break | % | 3.5 | 3.2 | |||
| Capacity | 600g set | 600g set | ||||
| 10kg/BIB | 10kg/BIB | |||||
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
Flexible type
| Y618LD | Y618H | Y630D | ||||||
|---|---|---|---|---|---|---|---|---|
| Agent A | Agent B | Agent A | Agent B | Agent A | Agent B | |||
| Application / Properties / Features | Flexible / Low distortion | Hight strength / High heat resistance | ||||||
| Base | Acrylic resin | Acrylic resin | Acrylic resin | |||||
| External appearance | Red | Blue | Light yellow | Light green | Light yellow | Light green | ||
| Viscosity | Pa･s/23°C | 5,000 | 5,000 | 15,000 | 15,000 | 4,000 | 4,000 | |
| Mixing ratio | 1:1 | 1:1 | 1:1 | |||||
| Pot life *1 | 23°C | 2 min | 2 min 30 s | 1 min 30 s | ||||
| Set time *2 | 23°C | 7 min | 10 min | 4 min 30 s | ||||
| Adhesive property | Tensile shear strength | MPa | 14.2 | 15.7 | 25.3 | |||
| T-peel strength | N/mm | 5.9 | 5 | 4.6 | ||||
| Curing properties | Hardness | Shore D | 47 | 55 | 83 | |||
| Glass transfer point | °C | 61 | 118 | |||||
| Elastic modulus | MPa | 451 | 2414 | |||||
| Breaking strength | MPa | 10.5 | 10.6 | 32.1 | ||||
| Elongation at break | % | 40 | 51 | 2 | ||||
| Capacity | 600g set | 190mL set | 600g set | |||||
| 10kg/BIB | ||||||||
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
Conventional type SGA Y650 (*Odorous)
| Y650 | ||||
|---|---|---|---|---|
| Agent A | Agent B | |||
| Base | Acrylic resin | |||
| External appearance | Blue | Red | ||
| Viscosity | mPa･s/23°C | 3,220 | 3,320 | |
| Mixing ratio | 1:1 | |||
| Pot life *1 | 23°C | 2 min 30 s | ||
| Set time *2 | 23°C | 4 min 30 s | ||
| Adhesive property | Tensile shear strength | MPa | 23.8 | |
| T-peel strength | N/mm | 4.6 | ||
| Curing properties | Hardness | Shore D | 60 | |
| Glass transfer point | °C | 83 | ||
| Elastic modulus | MPa | 740 | ||
| Breaking strength | MPa | 16.1 | ||
| Elongation at break | % | 25 | ||
| Capacity | 2.5kg | |||
*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).
| Price Terms: | fob Hongkong, fob Shenzhen |
|---|---|
| Payment Terms: | TT |