First, note
1, SGA for the second generation of degeneration of the acrylic-type structure of the two agents used then.
2, A / B two components are 100 percent solid, viscosity at 25 ℃ about 4000 cps.
3, use a ratio of 1:1.
4, Appearance: Danhong, red, transparent and translucent.
Second, identity
1, rapid hardening time, the summer about three minutes early can be fixed, while the winter until 5-8 minutes, 30 minutes after up to 80 percent strength, after a full 24 hours.
2, the metal objects of the then-resistant epoxy is superior impact strength.
3, heat and cold of excellent, high temperature 150 ℃ place for a week, also home at room temperature, the intensity of the same weak. -20 ℃ temperature at the end of the same strength of the weak.
4, weatherability: exposure to UV 200 hours under the intensity is still declining.
5, and then material: glass, Boli, metal, magnets, ceramics, wood, stone, plastic (PP, PE exception).
Third, to use
1, from A plastic 10 g and 10 g of plastic B uniform after mixing a paste.
2, A / B 2 has an adhesive coating on the surface, in line with a Self-stick adhesive surface.
3, A / B two points home Liang Tong, by air compressor pressure, the A / B two catheter, into mixed-automatic guns after the outflow of plastic coating, this method for the online operations of continuous use.
Four, note
1, A / B 2 to be stored in the shade, the two can not be at the same time Duizhi.
2, A / B as two large mixed, rapid curing dangerous, should be particularly cautious.
3, after use, such as skin Zhanfu of the agent, should be cleaned with soap.
4, coated tools, or containers can not be mixed each other, so as to avoid reducing the life of this agent.