Product Name: Polyester monofilament yarn for paper making industry
Material: 100% polyester
Specification: 0.20mm to 1.2mm
Luster: semidull
Color: raw white, varied dope dyed colors as per request.
Advantage and Characteristics: We specially equipped Germany standard extruding lines to produce the excellent quality polyester monofilament yarns for paper making industry. High tenacity, excellent diameter evenness, excellent friction endurance, low shrinkage.
End use and technical properties are as following:
1. Polyester monofilament for paper making forming fabric and dryer fabric --Weft Yarn
|
Model |
Diameter （mm） |
Diameter deviation (mm) |
Breaking strength (N) ≥ |
Tenacity (CN/Tex)， ≥ |
Elongation at break (%) |
Free shrinkage in hot air@ 180℃ x10min (%) |
|
VS50F |
0.22 |
±0.005 |
21 |
40 |
40±6 |
2±0.5 |
|
0.24 |
±0.005 |
25 |
40 |
40±6 |
2±0.5 |
|
|
0.25 |
±0.005 |
27 |
40 |
40±6 |
2±0.5 |
|
|
0.27 |
±0.005 |
32 |
40 |
40±6 |
2±0.5 |
|
|
0.30 |
±0.005 |
39 |
40 |
40±6 |
2±0.5 |
|
|
0.35 |
±0.006 |
53 |
40 |
40±6 |
2±0.5 |
|
|
0.38 |
±0.006 |
59 |
38 |
40±6 |
2±0.5 |
|
|
VS50R |
0.40 |
±0.01 |
66.0 |
38 |
40±6 |
3±0.7 |
|
0.45 |
±0.012 |
83.0 |
38 |
40±6 |
3.5±0.7 |
|
|
0.50 |
±0.015 |
92.0 |
34 |
40±6 |
3.5±0.7 |
|
|
0.55 |
±0.015 |
111.0 |
34 |
40±6 |
3.5±0.7 |
|
|
0.60 |
±0.015 |
129.0 |
33 |
40±6 |
3.5±0.7 |
|
|
0.65 |
±0.015 |
151.0 |
33 |
40±6 |
3.5±0.7 |
|
|
0.68 |
±0.015 |
165.0 |
33 |
40±6 |
3.5±0.7 |
|
|
0.70 |
±0.018 |
170.0 |
32 |
40±6 |
3.5±0.7 |
|
|
0.80 |
±0.02 |
222.0 |
32 |
40±6 |
3.5±0.7 |
|
|
0.90 |
±0.025 |
281 |
32 |
40±6 |
3.5±0.7 |
|
|
1.0 |
±0.03 |
336 |
31 |
40±6 |
4±1 |
|
|
1.1 |
±0.03 |
407 |
31 |
40±6 |
4±1 |
|
|
1.2 |
±0.03 |
484 |
31 |
40±6 |
4±1 |
Features :
Medium and high molecular, anti-hydrolysis, anti-dirty, low shrinkage and medium low shrinakge.
End use: as weft yarn for paper making fabric and dryer fabric.
2. Polyester monofilament for paper making forming fabric and dryer fabric--Warp Yarn
|
Model |
Diameter （mm） |
Diameter deviation (mm) |
Breaking strength (N) ≥ |
Tenacity (CN/Tex)， ≥ |
Elongation at break (%) |
Free shrinkage in hot air@ 180℃ x10min (%) |
|
VS60F |
0.20 |
±0.005 |
23.0 |
53 |
16±3 |
12±1 |
|
0.21 |
±0.005 |
25.0 |
53 |
16±3 |
12±1 |
|
|
0.22 |
±0.005 |
28.0 |
53 |
16±3 |
12±1 |
|
|
0.23 |
±0.005 |
31.0 |
53 |
16±3 |
12±1 |
|
|
0.25 |
±0.005 |
36.0 |
53 |
16±3 |
12±1 |
|
|
0.27 |
±0.005 |
42.0 |
53 |
16±3 |
12±1 |
|
|
0.30 |
±0.005 |
52.0 |
53 |
16±3 |
12±1 |
|
|
VS60R |
0.32 |
±0.006 |
59.0 |
53 |
16±3 |
12±1 |
|
0.35 |
±0.006 |
70.0 |
53 |
16±3 |
12±1 |
|
|
0.40 |
±0.001 |
92.0 |
53 |
16±3 |
12±1 |
|
|
0.65 |
±0.015 |
210.0 |
46 |
20±3 |
11±1 |
|
|
0.68 |
±0.015 |
230.0 |
46 |
20±3 |
11±1 |
Features :
Medium and high molecular, anti-hydrolysis, anti-dirty, high tenacity, medium shrinakge.
End use: as weft yarn for paper making fabric and dryer fabric.
3. Polyester monofilament for spiral net --Pin Yarn
|
Model |
Diameter （mm） |
Diameter deviation (mm) |
Breaking strength (N) ≥ |
Tenacity (CN/Tex)， ≥ |
Elongation at break (%) |
Free shrinkage in hot air@ 180℃ x10min (%) |
|
VS70A |
0.70 |
±0.018 |
175.0 |
33 |
30±5 |
8±1 |
|
0.80 |
±0.018 |
229.0 |
33 |
30±5 |
8±1 |
|
|
0.90 |
±0.02 |
272.0 |
31 |
30±5 |
8±1 |
|
|
1.0 |
±0.03 |
336.0 |
31 |
30±5 |
8±1 |
Features :
Medium molecular, medium shrinkage.
End use: as pin yarn for paper making spiral net.
4. Polyester monofilament for spiral net --Loop Yarn
|
Model |
Diameter （mm） |
Diameter deviation (mm) |
Breaking strength (N) ≥ |
Tenacity (CN/Tex)， ≥ |
Elongation at break (%) |
Free shrinkage in hot air@ 180℃ x10min (%) |
|
VS70B |
0.50 |
±0.015 |
114.0 |
42 |
19±3 |
17±1 |
|
0.60 |
±0.015 |
164.0 |
42 |
19±3 |
17±1 |
|
|
0.68 |
±0.015 |
185.0 |
37 |
19±3 |
17±1 |
|
|
0.70 |
±0.018 |
191.0 |
36 |
19±3 |
17±1 |
Features :
Medium molecular, high shrinkage.
End use: as loop yarn for paper making spiral net.