High performance ARC spraying cored wires
KX-99 ARC Spraying cored wire
Coating Types: High hardness and high wear-resistant amorphous coating
Main Chemical Components: Fe17Cr5NiB
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: Excellent.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): > 20
Coating microhardness (HV 0.1): > 1296
Coating hardness (HRC): > 60
Coating performance: High hardness, high wear resistance,
the coating containing lots of amorphous microcrystalline and nano-crystalline.
Typical application: High wear resistance. Preventing four tubes explosion of boiler. Circulation fluidized bed heating surface. Soot blowing port, fan blade. Converter hood & converter flue.
KX-90 ARC Spraying cored wire
Coating Types:high hardness and high wear-resistant coating
Main Chemical Components: Fe14Cr5NiB (Containing carbide ceramic particles)
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: Excellent.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): > 18
Coating microhardness(HV 0.1): > 1362
Coating hardness (HRC): > 60
Coating performance:
High hardness high wear resistance. High temperature oxidation resistance.
Typical application: High wear resistance. Preventing four tubes explosion of boiler. Soot blowing port,
Coal burner, fan blade. Converter hood & converter flue in steel plant.
KX-97 ARC Spraying cored wire
Coating Types: WC ceramic reinforced high wear-resistant coating
Main Chemical Components:FeCrNiBWC
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: Excellent.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): > 18
Coating microhardness(HV 0.1): 1023 ~ 1525
Coating hardness (HRC): > 60
Coating performance: There were WC ceramic hard phase in the coating
Typical application: High wear resistance protective material. Circulation fluidized bed boiler. Fan blade.
KX-60 ARC Spraying cored wire
Coating Types: High hardness and high wear resistant coating.
Main Chemical Components: FeCrNiBSi
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: Excellent.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): 18
Coating microhardness(HV 0.1): 1393
Coating hardness (HRC): > 60
Coating performance: High hardness high wear resistance
Typical application: circulation fluidized bed heating surface. Soot blowing fluidized bed boiler. Fan blade.
KX-70 ARC Spraying cored wire
Coating Types: High temperature erosion resistant coating.
Main Chemical Components:Fe23CrC (containing chromium carbide ceramic particles)
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: Excellent.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): >10
Coating microhardness(HV 0.1): 850
Coating hardness (HRC): > 60
Coating performance: High temperature oxidation and abtasive erosion resistance.
Typical application: Coal fired boiler four tubes repairing converter flue & Converter hood in steel plant
KX-96 ARC Spraying cored wire
Coating Types:High Chromium high temperature oxidation resistant coating
Main Chemical Components: Fe42Cr5BNi
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: Excellent.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): >10
Coating microhardness (HV 0.1): 800
Coating hardness (HRC): > 55
Coating performance: High temperature oxidation resistance high hot corrosion resistance. Excellent erosion and abrasion resistant.
Typical application: waste incinerator. Coal burner
KX-50 ARC Spraying cored wire
Coating Types: Martensitic stainless steel wear and corrosion resistant coating
Main Chemical Components: Fe Cr13NiAlRE
Adhesion Strength (Map): > 50 Mpa.
Abrasive wear resistance: good
Corrosion Resistance: good
Oxidation Resistance: good
Thermal shock Resistance: GOOD
Relative wear resistant (20G): >3
Coating microhardness(HV 0.1): 490
Coating hardness (HRC): > 48
Coating performance: High wear and corrosion resistance
Typical application: Coal-fired boiler four tubes. Repairing drying cylinder for paper-making, Crankshafts, plunger piston, shaft.
KX-40 ARC Spraying cored wire
Coating Types: Low carbon martensite high adhesive strength wear resistant coating.
Main Chemical Components: FeNiCrMoVAlRE
Adhesion Strength (Map): > 55 Mpa.
Abrasive wear resistance: Commonly.
Corrosion Resistance: commonly
Oxidation Resistance: commonly
Thermal shock Resistance: GOOD
Relative wear resistant (20G): --
Coating microhardness(HV 0.1): ---
Coating hardness (HRC): > 40
Coating performance: Low cost harmless and high effective. Optimal self-adhesion property. Wear resistance.
Typical application: Can be replace aluminum bronze and Ni-Al wires.
KX-NiCr3C2 ARC Spraying cored wire
Coating Types: Nickel base high temperature erosion and wear resistant coating
Main Chemical Components:NiCrC
Adhesion Strength (Map): > 55 Mpa.
Abrasive wear resistance: Commonly.
Corrosion Resistance: Excellent
Oxidation Resistance: Excellent
Thermal shock Resistance: GOOD
Relative wear resistant (20G): --
Coating microhardness(HV 0.1): 450
Coating hardness (HRC): > 46
Coating performance: High thermal shock resistance. Excellent high temperature erosion resistance and room high temperature wear resistance. The high temperature erosion resistance of coatings are found 15 to 20 times that of 20G under 750℃.
Typical application: Petroleum chemical industry. Excellent erosion and abrasion resistant material.