SmCo magnets are composed of Samarium, |
Cobalt, and a few transition metals. SmCo |
magnets are high performance, low temperature |
coefficient rare earth permanent magnets, and |
could keep their performance under the maximum |
working temperature 350 degree centigrade. |
Manufacturing Process |
Samarium, Cobalt, and a few transition |
metals will be made into the SmCo powder, |
then fine SmCo powder will be compacted in a |
die and sintered, fusing the powder into a solid |
material. There are 2 forms of pressing: die |
pressing and isostatic pressing. Sintered parts |
normallyneed some finish machining in order to |
meet final tolerances. |
Machining & Tolerance |
Generally, SmCo magnets must be machined |
using diamond-grinding techniques. Sometimes, |
machining operations may be performed on |
SmCo materials using carbide tools, but surface |
finishes thus obtained may be less than optimal. |
The Standard tolerances for SmCo magnets are |
+/- 0.1mm for ground dimensions, but sticter |
tolerances are possible if specially required. |
Surface treatments |
The corrosion resistance of SmCo magnets is |
considered good. Although Surface coating or |
plating is not generally required for SmCo magnets, |
all kinds of surface coating are also available, |
like Nickel, Zn, Ni-Cu-Ni, Gold, Silver, Sn,Chrome, |
ABS coating, Rubber coating, PTFE(Telfon) coating, |
stainless steel case, etc. |
Magnetizing & Packing |
SmCo magnets require extremely high magnetizing |
fields, and can be magnetized in any direction |
as long as it is aligned properly. In some instances |
multiple pole magnetization is possible with special |
fixtures. All SmCo magnets are anisotropic, and |
can only be magnetized in the orientation direction, |
so particular consideration must be given to this |
when designing complex assemblies, if it is intended |
to magnetize after assembly. |
SmCo magnets are mechanically weak, and |
magnetically very strong. They should be packed |
properly in order to help user to use and handle |
them. |