Product Description
|
Pure PTFE Sheet
Item:SINSTON ZR-40 |
Description: PTFE product includes sheet, Tube (SINSTON ZR-48), Rod (SINSTON ZR-49), Film (SINSTON ZR-47) and gaskets etc., they are molded, skived or cut from 100% virgin PTFE. It has the best chemical corrosion resistance among known plastics. Without being aging, lowest friction coefficient, wear resistance. The unloaded operating temperature range is -180~+260C.
CONSTRUCTION:
SINSTON ZR-41 Filled PTFE Sheet
The filled PTFE products are molded PTFE resin mixed with the most frequently used filler materials such as glass fiber, carbon fiber and graphite etc. The filled PTFE has improved compression strength, better abrasion resistance, high thermal conductivity and lower thermal expansion compared with pure PTFE products.
PROPERTIES & APPLICATION:
|
Style
|
Products
|
Tensile Strength
|
Pressure
Mpa
|
Density
g/cm3
|
Temperature
℃
|
|
SINSTON ZR-40
|
PTFE Sheet
|
15Mpa
|
10
|
2.1~2.3
|
-100 ~ 250
|
|
SINSTON ZR-41
|
Filled PTFE Sheet
|
10Mpa
|
16
|
2.1~2.3
|
-100 ~ 260
|
|
SINSTON ZR-45
|
EPTFE sheet
|
Gore, Klinger, Garlock, Sealon etc., According to manufacturer
|
Seal materials, electrical insulation parts, lining, oil less lubricating materials etc.
NORMAL DIMENSION:
|
Size(mm)
|
Thickness(mm)
|
tolerance
|
|
150X150
|
1.0~30
|
±0.30~±0.50
|
|
250X250
|
1.5~30
|
±0.30~±0.50
|
|
300X300
|
1.5~30
|
±0.30~±0.50
|
|
450X450
|
1.5~30
|
±0.30~±0.50
|
|
600X600
|
1.5~30
|
±0.30~±0.50
|
|
800X800
|
1.5~30
|
±0.30~±0.50
|
|
1000X1000
|
1.5~30
|
±0.30~±0.50
|
|
1200X1200
|
2~30
|
±0.30~±0.50
|
|
1000X2000
|
3~35
|
±0.30~±0.60
|
|
1500 X 1500
|
3~35
|
±0.30~±0.60
|
|
2000 X 2000
|
5~35
|
±0.30~±0.60
|
|
|
Product Image
Img 1
Img 2
Img 3
Img 4
Img 5
Img 6
Img 7
Img 8
Send Inquiry to this Member
Related Products of this Company
This member assumes full responsibility for the content of this listing. DIYTrade accepts no responsibility whatsoever in respect of such content.
To report fraudulent or illegal content, please
click here.
China Suppliers Quick Searching:
,