Product Description

Product Name

Biodegradable Starch Resin

 

Product Type

Film Blowing Grade Biodegradable Starch Resin

 

Product Features

Granules are in light yellow and come in cylinder and round shape, with slight fragrance. They absorb moisture easily and are easily decomposed by microbes. They are anti-static. The processing temperature of them is lower than that of conventional plastic. They are easily colored. Such resin can be processed into finish products directly, without adding any other polyolefin materials, like PE, PP, PVA, EVA, etc.

Product Testing

   Compliance with ISO148551999

   The degradation rate is more than 46% in 100 days.

   Test report from ChinaNationalCenter for Quality Supervision & Test of Plastics Products can be provided.

Properties and Data

 

BOR-Z–501F

Testing Item

Standard

Unit

Result

Appearance

Q/320113SSD001 - 2002

 

Light  Yellow

Density

GB 1033

g/ cm3

0.98 – 1.10

Moisture Content

Q/320113SSD001 - 2002

%

0.3 – 1.2

Melt Flow Index

GB3682

g/10 min

0 - 2

Tensile strength

GB 1040

MPa

≥12

Breaking Elongation

GB 1040

%

≥250

Bio Substances Content

Q/320113SSSD001 - 2002

%

≥55

n-hexane Extracts

GB/T5009.58

%

≤4.0

Softening Point

GB/1633

ºC

> 65

Degradation rate in100days

ISO14855:2000

%

> 46

The data for tensile strength and elongation refer to that of finished film products.

 

Recommended Applications

For all sorts of anti-static packing purposes, e.g. electronic product packaging, car interior covering film, electrical appliance packaging, agricultural mulch film, shopping bags, T-shirt bags, document folders, filter bags, storage bags, bin bags, tear-on-roll bags, disposable gloves, table cloths, aprons and rain coats, etc.

 

Processing Equipment

        Common film blowing extruder, sheet extruder, bags making machine, printers, and heat sealing machines are all can be used.

 

Processing Technology

   Best results will be achieved with a screw L/D ratio ≥ 28:1. The blow-up ratio should be more than 1:3 to achieve the maximum production yield and the best quality.

     BOR-Z-501F can be blended with LDPE to process film products.

     Newly made film feels brittle or crispy. Its elongation is low. This is due to severe dehydration during production. Therefore, the film needs to be settled for a 24- hour curing period to regain elongation and anti-tear strength before being used to make finish products, e.g. bag-making or printing.

  The minimum thickness of film made of such material can be 10 microns.

Remarks:

     Due to the high starch content, it easily absorbs moisture. Therefore, the package should be sealed properly to prevent the ingress of moisture.

     In case the resin is damp, it should be dried for 2 hours at 80ºC.

     The processing temperature will be lower 5-10 than that of PE. During processing, the temperature is correct when corn starch fragrance can be smelled at the hopper.

  It is extremely easily decomposed into the soil friendly substances in the microbial environment.

 


Product Image

BOR-Z-501F 1
Img 1
BOR-Z-501F 2
Img 2

Send Inquiry to this Member

Guangdong Shangjiu Biodegradable Plastics Co.,Ltd.

Shangjiu Environmental Protection Eco-Technology Industrial Park,Niushan, Dongcheng District, Dongguan City, Guangdong, China

Phone:
086-769-22114999
Fax:
086-769-22103988
Contact:
Mr Fan Yuhui (Sales Executive)
Mobile:
13538306020

Related Products of this Company

This member assumes full responsibility for the content of this listing. DIYTrade accepts no responsibility whatsoever in respect of such content.
To report fraudulent or illegal content, please click here.

China Suppliers Quick Searching:

High Polymers Made In China Products

,  

High Polymers China Suppliers and China Manufacturers