Subcategory: Polycarbonate; Polymer; Thermoplastic
Close Analogs: Saudi Basic Industries Corporation (SABIC) announced on August 31st, 2007, the completion of its purchase of GE Plastics.
Material Notes:
Information provided by GE Plastics for their North American product line.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
Physical Properties | Metric | English | Comments | |
|
||||
Density | 1.18 g/cc | 0.0426 lb/in� | ASTM D 792 | |
Mechanical Properties |
||||
|
||||
Tensile Strength @ Break | 57.2 MPa | 8300 psi | Type I, 2.0 in/min; ASTM D 638 | |
Tensile Strength @ Yield | 57.2 MPa | 8300 psi | Type I, 2.0 in/min; ASTM D 638 | |
Elongation at Break | 103 % | 103 % | Type I, 2.0 in/min; ASTM D 638 | |
Tensile Modulus | 1.59 GPa | 230 ksi | 2.0 in/min; ASTM D 638 | |
Flexural Modulus | 1.83 GPa | 266 ksi | 0.05 in/min, 2" span; ASTM D 790 | |
Flexural Yield Strength | 75.2 MPa | 10900 psi | 0.05 in/min, 2" span; ASTM D 790 | |
Izod Impact, Notched, Low Temp | 4.81 J/cm | 9 ft-lb/in | at -22F; ASTM D 256 | |
Gardner Impact @ 23�C | 70.6 J | 52.1 ft-lb | Instrumented Impact Total Energy, 73�F; ASTM D 3763 | |
Izod Impact, Notched | 5.66 J/cm | 10.6 ft-lb/in | 73F; ASTM D 256 | |
Thermal Properties |
||||
|
||||
Deflection Temperature at 1.8 MPa (264 psi) | 116 �C | 240 �F | 0.250 inch, unannealed; ASTM D 648 |