Category

类 别

Trade
mark

牌 号

Chemical composition

主要成份(%)

Characteristics & application

特性和用途

Equivalent to AWS

相当AWS

Hardfacing

硬

面

堆

焊

S101耐磨焊丝

C3 Cr28 Ni4
Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，耐磨、耐气蚀、抗氧化。堆焊铲斗齿，泵套

S111钴基焊丝

C1 Cr29 W5
Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高温下耐磨、耐蚀。堆焊高温高压阀门

ECoCr-A

S112钴基焊丝

C1.5 Cr29 W8
Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高温下耐磨、耐蚀。堆焊阀门，热轧孔型

ECoCr-B

S113钴基焊丝

C2.5 Cr30 W17
Co Rem.

HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高温下耐磨、耐热，但抗冲击性差。堆焊螺旋送料机用

S114钴基焊丝

C2.5 Cr30 W12
Co Rem.

HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高温下耐磨、耐热，但抗冲击较差。堆焊牙轮钻头

ECoCr-C

Copper

alloys

铜

合

金

S201铜合金焊丝

Sn1 Si0.3Mn0.3
Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
机械性能好，抗裂性好。紫铜气焊及氩弧焊用

ERCu

S211铜合金焊丝

Si3 Mn1
Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
机械性能好，铜合金氩弧焊及钢的MIG钎焊用

ERCuSi-Al

S212铜耐磨焊丝

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。铜合金氩弧焊及钢的堆焊用

ERCuSn-A

S213铜耐磨焊丝

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。铜合金氩弧焊及钢的堆焊用

ERCuSn-C

S214铜耐磨焊丝

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

ERCuAl-A1

S215铜耐磨焊丝

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

ERCuAl-A2

S221铜合金焊丝

Cu60 Sn1 Si0.3
Zn Rem.

Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

S221F铜合金焊丝

Cu60 Sn1 Si 0.3
Zn Rem.

S221 welding rod coated with flux.
外涂焊剂的S221焊丝

S222铜合金焊丝

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

RBCuZn-C

S222F铜合金焊丝

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

S222 welding rod coated with flux.
外涂焊剂的S222焊丝

RBCuZn-C

S223铜合金焊丝

Cu59 Sn0.6
Zn Rem.

Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔点约900℃。铜、钢、铸铁钎焊用

RBCuZn-A

S224铜锌焊丝

Cu62 Si0.5
Zn Rem.

Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

Copper
alloys

铜

合

金

S225铜锌焊丝

Cu48 Ni10
Zn Rem.

Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔点约935℃。高强度,钎焊钢、镍及硬质合金用

RBCuZn-D

S225F铜锌焊丝

Cu48 Ni10
Zn Rem.

S225 welding rod coated with flux.
外涂焊剂的S225焊丝

RBCuZn-D

S226铜锌焊丝

Cu60 Sn0.3
Si0.2 Zn Rem.

Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁

S227铜锌焊丝

Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

RBCuZn-B

S229铜锌焊丝

Cu55 Ni6 Mn4
Zn余

Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔点约920℃。高强度,钎焊钢、镍及硬质合金用

Aluminum alloys

铝

合

金

S301纯铝焊丝

Al≥99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蚀。纯铝气焊、氩弧焊用

ER1100

S311铝镁焊丝

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金

ER4043

S321铝焊丝

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用

S331铝焊丝

Mg5 Mn0.4
Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蚀，强度高。铝合金氩弧焊用

ER5183<