Die Shear Strength (Si to Cu L/F) @ RT (58×50mil2) @ 250°C (250×250mil2) |
> 7.0 kg > 3.0 kg |
BHS-K-109 |
Hot-Wet Die Shear Strength after 85%/85°C/24hr @250°C(80×80mil2) |
1.8 kg |
BHS-K-109 |
DSC
|
Onset 162 °C Peak 163 °C |
BHS-K-113 |
Glass Transition Temp. (Tg) |
99.5 °C |
BHS-K-116 |
Ionic impurity Chloride Sodium Potassium |
≤ 15 ppm ≤ 10 ppm ≤ 10 ppm |
BHS-K-104 |
Thermal Conductivity |
> 20 W / m.k |
- |
TMby Expansion @α1 @α2 |
35 ppm 120 ppm |
BHS-K-117 |
Modulus @ 25℃ @ 100℃ @ 250℃ |
60 MPa 42 MPa 68 MPa |
BHS-K- |