Category

類 別

Trade
mark

牌 號

Chemical composition

主要成份(%)

Characteristics & application

特性和用途

Equivalent to AWS

相當AWS

Hardfacing

硬

面

堆

焊

S101耐磨焊絲

C3 Cr28 Ni4
Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊剷斗齒，泵套

S111鈷基焊絲

C1 Cr29 W5
Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高溫下耐磨、耐蝕。堆焊高溫高壓閥門

ECoCr-A

S112鈷基焊絲

C1.5 Cr29 W8
Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高溫下耐磨、耐蝕。堆焊閥門，熱軋孔型

ECoCr-B

S113鈷基焊絲

C2.5 Cr30 W17
Co Rem.

HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高溫下耐磨、耐熱，但抗衝擊性差。堆焊螺旋送料機用

S114鈷基焊絲

C2.5 Cr30 W12
Co Rem.

HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高溫下耐磨、耐熱，但抗衝擊較差。堆焊牙輪鑽頭

ECoCr-C

Copper

alloys

銅

合

金

S201銅合金焊絲

Sn1 Si0.3Mn0.3
Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
機械性能好，抗裂性好。紫銅氣焊及氬弧焊用

ERCu

S211銅合金焊絲

Si3 Mn1
Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
機械性能好，銅合金氬弧焊及鋼的MIG釬焊用

ERCuSi-Al

S212銅耐磨焊絲

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。銅合金氬弧焊及鋼的堆焊用

ERCuSn-A

S213銅耐磨焊絲

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。銅合金氬弧焊及鋼的堆焊用

ERCuSn-C

S214銅耐磨焊絲

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用

ERCuAl-A1

S215銅耐磨焊絲

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用

ERCuAl-A2

S221銅合金焊絲

Cu60 Sn1 Si0.3
Zn Rem.

Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

S221F銅合金焊絲

Cu60 Sn1 Si 0.3
Zn Rem.

S221 welding rod coated with flux.
外塗焊劑的S221焊絲

S222銅合金焊絲

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

RBCuZn-C

S222F銅合金焊絲

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

S222 welding rod coated with flux.
外塗焊劑的S222焊絲

RBCuZn-C

S223銅合金焊絲

Cu59 Sn0.6
Zn Rem.

Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔點約900℃。銅、鋼、鑄鐵釬焊用

RBCuZn-A

S224銅鋅焊絲

Cu62 Si0.5
Zn Rem.

Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

Copper
alloys

銅

合

金

S225銅鋅焊絲

Cu48 Ni10
Zn Rem.

Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔點約935℃。高強度,釬焊鋼、鎳及硬質合金用

RBCuZn-D

S225F銅鋅焊絲

Cu48 Ni10
Zn Rem.

S225 welding rod coated with flux.
外塗焊劑的S225焊絲

RBCuZn-D

S226銅鋅焊絲

Cu60 Sn0.3
Si0.2 Zn Rem.

Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵

S227銅鋅焊絲

Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

RBCuZn-B

S229銅鋅焊絲

Cu55 Ni6 Mn4
Zn余

Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔點約920℃。高強度,釬焊鋼、鎳及硬質合金用

Aluminum alloys

鋁

合

金

S301純鋁焊絲

Al≥99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蝕。純鋁氣焊、氬弧焊用

ER1100

S311鋁鎂焊絲

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金

ER4043

S321鋁焊絲

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用

S331鋁焊絲

Mg5 Mn0.4
Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蝕，強度高。鋁合金氬弧焊用

ER5183<