T1 47-52HRC akv>=16J >=1499Mpa >=3% >=1040N/mm2 
T2 48-52HRC akv>=20J >=1500Mpa >=4% >=1100N/mm2 
T3 48-52HRC akv>=20J >=1550Mpa >=5% >=1100N/mm2 

For general purpose we recommend Grade 2 which is both strong and wear long. 
For Grade 1 material, we reduce the alloy composition,therefore the wear life is 2/3 of Grade 2. 
And our Grade 3 is ESCO material which wear 1.3 times of Grade 2.