Super X Gold No.777

Features

1. Fast curing 
   Handling time by the open time about 1 min after application : About 1-2 min./23°C 
   Handling time by the open time about 2 min after application : About 30 sec.-1 min./23°C 
   Good low-temperature curing 
    
2. Environmental countermeasure products 
   Avoidance of 14 substances formulated based on the guidelines of the Ministry of Health, Labour and Welfare 
   Avoidance of poisonous and deleterious substances 
   Voluntary registration of products not subject to formaldehyde by the Japan Adhesive Industry Association [Conformity to JAIA F☆☆☆☆･4VOCStandards] 
   Rohs Compliant products 
    
3. High durability 
   Excellent thermal shock resistance and high durability

Application

• For adhesive applications that require initial adhesive strength
• For bonding applications where durability is required by repeated heating, cooling and vibration

Property

			Super X Gold No.777
			White	Black	Clear
Application / Properties / Features			High-Speed curing type
Type			One component type Elastic Adhesive
Base			Special polymer containing silyl group
Appearance			White-Whitish Yellow paste  (Curing: White)	Black Paste(Curing: Black)	Light yellow clear paste  (Curing: Light yellow)
Viscosity		Pa･s/23°C	82.0	82.6	76.0
Specific gravity		g/cm3	1.14	1.14	1.02
Skin over time		23°C	2.5 min.	2.5 min.	3.5 min.
Adhesive property	Tensile shear strength	MPa	3.2	3.2	5.9
	T peel strength	N/mm	3.31	3.31	3.08
Curing properties	Hardness	Shore A	58	58	60
	Breaking strength	MPa	3.42	3.42	3.65
	Elongation at break	%	120	120	110
Electrical characteristics	Volume resistivity	Ω･cm	3.5 x 1012	3.5 x 1012	2.3 x 1012
	Dielectric constant	100Hz	5.12	6.30	3.87
	Dielectric loss tangent	100Hz	0.19	0.28	0.07
Grade
Capacity			135mL	135mL	135mL