Model: | CM135B |
---|---|
Brand: | Yaxin |
Origin: | Made In China |
Category: | Chemicals / Rubber Materials |
Label: | CPE135B , CPE , Rubber CPE |
Price: |
US $1570
/ MT
|
Min. Order: | 15 MT |
Plastic Modification CPE (PVC auxiliary, plasticizer, stabilizer, modifier)
YAXIN CPE 135A (max 5 pct Calcium Content)
Chlorinated Polyethylene Resin
YAXIN CPE 135A Resin is a low viscosity chlorinated polyethylene with low crystallinity.
A plastic rigid product modifier, mainly used for producing window profiles, UPVC water pipe & sewer pipe, cold curved pipe, PVC blowing board and PVC extrusion board, to achieve better plastification and anti-agglomeration performance.
No. |
Physical Property |
Unit |
Nominal Value |
Test Method |
||
GB/T |
ISO |
|||||
1 |
Chlorine Content |
% |
35±2 |
GB/T7139 |
ISO1158 |
|
2 |
Heat of Fusion |
(J/G) |
≤2.0 |
GB/T19466 |
ISO11357 |
|
3 |
Volatile Matter |
% |
≤0.40 |
GB/T2914 |
ISO1269 |
|
4 |
Sieve Residue(0.9mm sieve pore) |
% |
≤2.0 |
GB/T21843
|
ISO22498
|
|
5 |
Number of Colored Particles (Pieces/100g) |
Pieces |
≤50 |
Xinda Method |
Xinda Method |
|
6 |
Ash Content |
% |
≤4.5 |
GB/T9345.1 |
ISO3451-1 |
|
7 |
Tensile Strength |
Mpa |
≥8.0 |
GB/T528 |
ISO37 |
|
8 |
Shore Hardness |
Shore A |
≤65 |
GB/T531.1 |
ISO7619-1 |
|
9 |
Elongation at Break |
% |
≥600 |
GB/T528 |
ISO37 |
|
10 |
Apparent Density |
g/ml |
≥0.45 |
Xinda Method |
Xinda Method |
|
11 |
Whiteness |
% |
≥80 |
Xinda Method |
Xinda Method |
|
12 |
Calcium Content |
% |
≦5.0 |
Client's demand |
Client's demand |
|
Note: These properties are typical but do not constitute specifications. Users should confirm results by their own test. |
||||||
weifang xinda chemical co., ltd | |
---|---|
Country/Region: | Shan Dong - China |
Business Nature: | Manufacturer |
Phone: | 18653625821 |
Contact: | Richardlee (Marketing Manager) |
Last Online: | 31 Dec, 2012 |