Property

Unit

Test Method

Test Condition

AG12A0

Tensile Strength

kg/cm2
( MPa)

ASTM D-638
( ISO527)

23℃

510

(50)

Flexural Strength

kg/cm2
( MPa)

ASTM D-790
( ISO178)

23℃

750

(74)

Flexural Modulus

kg/cm2
( MPa)

ASTM D-790
( ISO178)

23℃

25000

(2450)

Rockwell
Hardness

　R-Scale

ASTM D-785
( ISO2039/2 )

23℃

R-106

Izod
Impact Strength

kg-cm/cm
( J/m )

ASTM D-256
( ISO R180 )

23℃
1/4'' bar

30

(294)

Vicat Softening
Temperature

℃

ASTM D-1525 
(ISO 306)

1Kg load

103

Heat Deflection
Temperature

℃

ASTM D-648
(ISO 75/A)

Unannealed
18.6kg/cm2
( 1/2'' bar )

88

Annealed
( 80℃×8Hr )

100

Melt 
Flow Index

g/10 min

ASTM D-1238
( ISO1133 )

200℃×5Kg
( 49N )

1.6

220℃×10Kg
( 98N )

17

Molding 
Shrinkage

%

FCFC Method

23℃

0.4~0.7

Specific Gravity

ASTM D-792
( ISO1183 )

23℃/23℃

1.04

Flammability

UL-94

FILE NO.
E162823

1/16" HB

All Color