Property

Unit

Test Method

Test Condition

Tensile Strength

kg/cm2
( MPa)

ASTM
D-638
( ISO527)

23℃

220

(22)

Tensile Elongation

%

ASTM
D-638
( ISO527)

23℃

40

Flexural Strength

kg/cm2
( MPa)

ASTM
D-790
( ISO178)

23℃

440

(43)

Flexural Modulus

kg/cm2*104
( MPa)

ASTM
D-790
( ISO178)

23℃

2.3

(2260)

Izod
Impact Strength

kg-cm/cm
( J/m )

ASTM
D-256
( ISO R180 )

23℃
1/4'' bar

11.0

(108)

Vicat Softening
Temperature

℃

ASTM
D-1525
(ISO306B)

Annealed
80℃×2Hr
1/8'' bar

95

Heat Deflection
Temperature

℃

ASTM
 D-648
( 75/A)

Annealed
80℃×2Hr
1/8'' bar

88

Melt
Flow Index

g/10 min

ASTM
D-1238
( ISO1133 )

200℃×5Kg
( 49N )

5.5

Residual Monomer

ppm max.

700

Molding 
Shrinkage

%

FCFC
Method

23℃

0.4~0.6

Specific Gravity

ASTM
D-792
( ISO1183 )

23℃/23℃

1.04

Flammability

UL-94

FILE NO.
E162823

1/16" HB

NC