Nylon/ Flame Retarded Resin PA66
| Model: | QX-014 |
|---|---|
| Brand: | QX |
| Origin: | Made In China |
| Category: | Chemicals / Plastic Materials |
| Label: | Nylon/ Flame Retarde , plastic chemcials , polymer |
| Price: |
-
|
| Min. Order: | - |
Product Description
improved flame retardance and enhanced long-term performance. Flame retardant based on nitride ; outstanding mechanical and electrical properties.
| TEST ITEMS | TEST METHOD AND CONDITIONS | TEST RESULTS | ||
| TEST METHOD | UNIT | CONTITIONS | ||
| (DRY)23 | ||||
| Density | ISO1183 | g/cm3 | 1.1 | |
| Melt Volume Rate | ISO1133 | cc/10min | (275)2.16kg | 43.2 |
| Tensile Strength | ISO527 | MPa | 10mm/min | 67.8 |
| Tensile strain at break | ISO527 | % | 5 | |
| Flexural Modulus | ISO178 | MPa | 2,800 | |
| Flexural Strength | ISO178 | MPa | 2mm/min | 82 |
| Charpy Notched | ISO179 | KJ/m2 | 2.9m/s-1J | 11 |
| Izod Notched Impact | ISO180 | KJ/m2 | 3.5m/s-1J | 8.6 |
| Flame resistance | UL-94 | V-0 | ||
| Processing Guidelines | ||||
| Material Handling
Max. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficient |
||||
| Typical Profile
Melt Temperature 250-280°C (482-536 °F) Mold Temperature 60-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi) |
||||
| Fill Rate
Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate |
||||
Member Information
| Handan Hanshan Jinteng Trading Co. Ltd | |
|---|---|
| Country/Region: | Shan Dong - China |
| Business Nature: | Manufacturer |
| Phone: | 13722378488 |
| Contact: | Bonnie (Sales manager) |
| Last Online: | 13 Nov, 2013 |