Metal content

C:5%,Cr:27-30%,Martensite matrix and Cr7C3 carbides above 60%

Hardness 

Macro hardness of alloy layer HRC57-65, carbide hardness HV1400-1800

Wear resistance

20-25 times than low carbon steel,8-12 times than stainless steel and high manganese steel ,1.5 times than the 
general chromium carbon steel.

Temperature resistance

Common lower than  600 degrees; high temperature lower than 1000 degrees

Impact resistance

Wear resistant alloy layer metallurgically combine with the substrate completely,
resistance to strong impact,do not need to worry about shedding

Workability

Can be welded,cut,folded,drilled