Q1-Test QSS-270 Description:
Salt Spray Test Chambers QSS-270 offer the most realistic and dependable corrosion test, widely used to test corrosion resistance of automotive, paint, surface coating, chemical, aerospace, electronic, car industry, offshore and defense industries.


Q1-Test Features:

1, QSS-270 chamber material is made of P.V.C Sheet, sturdily and will not be out of shape.

2, QSS-270 test chamber is heated from five directions to ensure the temperature is uniformity distributed.

3, QSS-270 spray nozzle is specially made, enable to spray the salt water with considerable speed, then falls on the surface of samples.

4, Hot and moist air keeps the humidity in the QSS-270 test chamber conforms testing request.

5, High precision P.I.D. temperature controller limits the temperature difference within the range of ±0.1℃QSS-270.


Q1-Test QSS-270 Specifications：

Ambient Temp. and Humid. Range: +5℃ ~ +35℃ / <85%RH

Testing Temperature: NSS ACSS 35℃±1℃ / CASS 50℃±1℃

Air Temperature: NSS ACSS 47℃±1℃ /CASS 63℃±1℃

Solution Consistence: NaCi 5%

PH Value: NASS ACSS 6.5~7.2; CASS 3.0~3.2

Temperature Fluctuation: ≦±0.5℃

Temperature Uniformity: ≦2. 0℃

Temperature Deviation: ≦±2.0℃

Spray Quantum: 1.0~2.0(ml/80cm2/h)

Chamber Material: Polyvinyl chloride (PVC)

Heater: Corrosion-resistant titanium tube

Temperature Sensor: Platinum Resistance (PT-100)

Safety Device: Over-temperature protection , leakage protection

Specifications：

Model		QSS-108	QSS-270	QSS-510	QSS-816		QSS-1200
Interior dimensions (mm)	W	600	900	1200	1600		2000
	D	450	600	850	850		1000
	H	400	500	500	600		600
Exterior dimensions (mm)	W	1130	1460	2200	2600		3000
	D	630	910	1200	1450		1650
	H	1070	1280	1450	1550		1600
Solution Tank		15L	25 L	60 L
Power Supply		AC 220V/50HZ/1P				AC 380V/50HZ/3P
Ambient temp. & humid. range		+5℃ ~ +35℃ / <85%RH
Testing Temperature		NSS ACSS 35℃±1℃ / CASS 50℃±1℃
Air Temperature		NSS ACSS 47℃±1℃ /CASS 63℃±1℃
Solution Consistence		NaCi 5%
PH Value		NASS ACSS:6.5~7.2  / CASS:3.0~3.2
Temperature fluctuation		± 0.5℃
Temperature uniformity		≦2. 0℃
Temperature Resolution		0.1℃
Spray quantum		1.0~2.0(ml/80cm2/h)
Chamber Material		polyvinyl chloride  (PVC)
Heater		Corrosion-resistant titanium tube
Temperature sensor		Platinum Resistance (PT-100)
Safety device		Over-temperature protection , leakage protection

Note:

1. The above specifications are for reference only, the actual specifications for the main quotation.

2. Custom made is available according to customers’ special requirements

 

Salt Spray Test Chamber Conform But Not Limited Following Testing Standards:

※ ASTM B117 Standard Practice for Operating Salt Spray Apparatus

※ ASTM B368-97 Standard Method for Copper-Accelerated Acetic Acid-Salt Spray (Fog) Testing (CASS Test)

※ ASTM B380-97(2007) Standard Test Method of Corrosion Testing of Decorative Electrodeposited Coatings by the Corrodkote Procedure

※ ASTM D1735-99 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus

※ ASTM G85 - 11 Standard Practice for Modified Salt Spray (Fog) Testing

※ SGM-GM4465P Water Fog Humidity Test

※ ISO7253:2001 Paints and varnishes – Determination of resistance to neutral salt spray (fog)

※ ISO9227-2012 Corrosion tests in artificial atmospheres – salt spray tests

※ DIN 50021: Salt spray testing

※ JIS Z2371 Methods of Salt Spray Testing