RTV-2 Liquid Mold Making Silicone for Resin Crafts

Model:	E-620 silicone
Brand:	hong ye silicone
Origin:	Made In China
Category:	Chemicals / Rubber Materials
Label:	silicone for resin , RTV-2 silicone , silicone rubber
Price:	US $12.68 / pc
Min. Order:	200 pc

Inquire Now

Product Description

RTV-2 Liquid Mold Making Silicone For Resin Crafts Description:

Silicone Mold Making Material/Silicone for Mold Making are generally named as two-part addition silicone rubber that vulcanizes at room temperature. Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity, good operability, excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.

Silicone Mold Making Material/Silicone For Mold Making Main application:

Rapid prototyping (urethane casting/silicone tooling/vacuum casting)
Concrete moulding
PU resin casting
General Mouldmaking
Superior manual mold design

Silicone Mold Making Material/Silicone For Mold Making Main properties:

almost nil shrinkage
high chemical resistance to aggressive components of some types of resins
good tear strength (this feature ensures higher resistance to wearing and shearing)
high degree of precision in reproduction
high dimensional stability over time and non-deformability
high resistance to high temperatures and ageing (resit to -60-200°C)
excellent non-stick effect
environmental, odorless and nontoxic

RTV-2 Liquid Mold Making Silicone For Resin Crafts standard datasheet (25°C)(A:B=1:1 mixing ratio)

Product	E-620	E-625	E-630	E-642	E-647
Appearance	Translucent	Translucent	Translucent	Translucent	Translucent
Hardness(shore A)	20±2	25±2	30±2	42±2	47±2
Mix ratio(A:B)	1:1	1:1	1:1	1:1	1:1
Viscocity Part A(mPa.s)	23000±2000	27000±2000	25000±2000	30000±2000	35000±2000
Viscocity Part B(mPa.s)	3500±500	3500±500	2400±500	6000±500	3200±500
Tensile strength (kgf/cm²)	38±5	48±5	50±5	65±5	65±5
Tear-strength (kN/m)	16±2	16±2	16±2	16±2	16±2
Elongation(%)	500±50	500±50	450±50	450±50	450±50
Pot life/working time (mins)	30-40	30-40	30-40	30-40	30-40
Curing time/setting time (hrs)	3-4hrs(25°C) 110-20mins(60°C)	3-4hrs(25°C) 110-20mins(60°C)	3-4hrs(25°C) 110-20mins(60°C)	3-4hrs(25°C) 1 110-20mins(60°C)	3-4hrs(25°C) 10-20mins(60°C)
Shrinkage rate (%)	0.1	0.1	0.1	0.1	0.1

RTV-2 Liquid Mold Making Silicone for Resin Crafts is widely used in rapid prototyping industry, typically used for making 20 to 40 pieces of functional prototypes out of broad range of polyurethanes and other polymers. silicone tooling is the fastest, most accurate, and least expensive way to create duplicates of a prototype part .Merchandise made in our addition silicone moulds have a high quality analogous to the final product, which makes them particularly advisable for fit and performance testing and advertising purposes.

Notice:

All above addition silicone is forbidden to mix with organic compounds of condensation cure silicone rubber, otherwise, the silicone rubber will not cure, and also should not mix with organic compounds containing S, P, N as well as metallic salt of organic acids. It also will cause this product cure incompletely or not cure

For getting further information about silicone rubber, PLS contact with

Ms Bella:
Email: hysi(at)szrl(dot)net
Skype: bellajiaqi
Tel: 86-755-89948006
Mob: 86-18938867572