Key Specifications/Special Features:

· Potassium Titanyl Phosphate (KTiOPO4 or KTP) is widely used in both commercial and military lasers including laboratory and medical systems, range-finders, lidars, optical communication and industrial systems.

· HG’s KTP crystals are featured by:

· Large nonlinear optical coefficient

· Wide angular bandwidth and small walk-off angle

· Broad temperature and spectral bandwidth

· High electro-optics coefficient and low dielectric constant

· Non-hygroscopic, chemically and mechanically stable

· Basic properties:

· Crystal Structure Orthorhombic, space group Pna21,point group mm2

· Lattice Parameter a=6.404?, b=10.616?, c=12.814?, Z=8

· Melting Point About 1172°C

· Mohs Hardness 5

· Density 3.01 g/cm3

· Thermal Conductivity 13W/m/K

· Thermal Expansion Coefficient αx=11x10-6/°C, αy=9x10-6/°C, αz=0.6x10-6/°C

· HG Optronics INC. Warranty on specifications:

· Dimension tolerance: (W±0.1mm)x(H±0.1mm)x(L+0.5/-0.1mm) (L≥2.5mm)

· (W±0.1mm)x(H±0.1mm)x(L+0.1/-0.1mm) (L<2.5mm)

· • Clear aperture: central 90% of the diameter

· • No visible scattering paths or centers when inspected by a 50mW green laser

· • Flatness: less than λ/8 @ 633nm

· • Transmitting wavefront distortion: less than λ/8 @ 633nm

· • Chamfer: ≤0.2mm@45°

· • Chip: ≤0.1mm

· • Scratch/Dig code: better than 10/ 5 to MIL-PRF-13830B

· • Parallelism: better than 20 arc seconds

· • Perpendicularity: ≤5 arc minutes

· • Angle tolerance: Δθ≤0.25°, Δφ≤0.25°

· • Damage threshold[GW/cm ]: >0.5 for 1064nm, TEM00, 10ns, 10HZ (AR-coated)

· >0.3 for 532nm, TEM00, 10ns, 10HZ (AR-coated)

· HG provides the following AR coating specifications:

· AR-(1064/532) nm. R <0.2% @1064nm and R <0.5%@ 532nm

· Damage threshol t; 300MW/cm2 @ 1064,532 nm 0MW/cm2 @ 1064,532 nm

· Broadband AR coating

· HR1064nm & HT532nm, R> 99.8% @ 1064nm, T> 90% @ 532nm.