Headtech half sleeve clamp is mainly used for stopping leakage of the petroleum and gas piping line.

Headtech Steel Half repair sleeve clamp is designed to avoid a costly shut down.  Existing lines can be cased without thru-put loss, because it is not necessary to shut down the carrier line to perform the required repair.  A full scope of sizes, ASTM grades of steel plate (structural and pressure vessel quality), wall thickness and longitudinal edge options are available.  Half  repair Sleeve clamp, also called split casing or half wrap, are custom-fabricated to your specifications, to assure a precision product and secure fit.

Half sleeve clamp is not a stock item. Every order is custom made.

When inquiring about this product,
please provide the following information:

Carrier pipe O.D.
Grade of steel plate
Wall thickness
Type of longitudinal edge (contact us for options)
Total footage required specifying the total footage as Half Sole or Full Wrap
Material
Material used to form Half Sole are from Chinese famous steel company, stock structural quality carbon steel or pressure vessel quality carbon steel plates, which are to ASTM specifications, and in the following grades:

ASTM A36 (structural; minimum yield 36,000 psi)
ASTM A572 GR50 (structural; minimum yield 50,000 psi)
ASTM A572 GR65 (structural; minimum yield 65,000 psi)
ASTM A516 GR70 (pressure vessel; minimum yield 38,000 psi)
ASTM A537 Class I (pressure vessel; minimum yield 50,000 psi) [limited stock]
The chemical composition does not exceed the percentages specified for the ASTM material ordered. Repair sleeves are fabricated from plate with low carbon equivalency for good weldability.

The maximum allowable carbon equivalency (CE) of Headtech' stock structural quality carbon steel plates will be based on the heat analysis.

The maximum allowable carbon equivalency (CE) of Headtech' stock pressure vessel quality carbon steel plates will be based on the heat analysis, in most cases.

Upon receipt of stock steel plates, heat numbers will be checked and verified with the material test reports. Copies of material test reports will be kept on file and will be used to recheck and re-verify heat numbers prior to cutting material in first step of manufacture.

Manufacturing
Half Sole is formed by rolling, step braking, or die forming without the use of heat treating.

Longitudinal edges of the Half Sleeve clamp are beveled for welding, if requested, at 30º. The bevel are a mechanical type and/or produced by plasma torch burning.

Half sleeve clamp ends have sheared square edges for fillet welding, unless square end bevel is requested, and are available in maximum lengths of: