Super-ferritic stainless steel Grade 439

Technical advantages:
Producing advantage: Equipped with large-scale, advanced and high efficient equipments, we can produce a series of super ferritic stainless steel product is in different grades and specifications, and meet the requirements of market.
Quality of products: The process which use hot metal as main part of materials to produce super ferritic stainless steel can reduce the unnecessary elements to lowest level. Using VOD decarburization and denitrifying process can get the lower content of carbon and nitrogen.

Application of Super Ferritic Stainless Steel Industry

The industry of automobile exhausting system: We have established long term cooperation with end users and service centers which work at automobile exhausting tubes and pressed parts.

Conventional Products
Steel grade Grade Specifications
Thickness Width mm Weight MT Standard Application
400 series 439
TTS439 2B/2D Surface: 0.3-3.0mm

BA surface: 0.2-1.5mm 2B/2D Surface:
1000-1280
1000-2000

BA surface: 1000-1500 6-15MT ASTM/ASME
Q/T 012-2011 Apply to elevator, kitchen appliance

Chemical Composition

Grade Mass Percentage (%)  MAX
 C Si Mn P S Cr N Mo Others
439 0.030 1.00 1.00 0.040 0.015 17.5-18.5 0.030 - Nb+Ti:4C-0.75

Physical properties
Grade Density (g/cm3) Elastic modulus GPa    Linear expansion coefficient 10-6/K20-100C    Themnal conductivity W/m K 100C    J/Kg k Specific heat 20C    Resistance rate (UM cm)    Magnetism
439    7.70    200    10.4    23.1    460    60    Qualified

Mechanical Properties
Mechanical properties at ambient temperature
Grade Yield strength RP0.2(MPa)      Tensile strength Rm(MPa)     Elongation A(%)     Hardness HRS     Hardness HV     Bending test
439  ≥205  ≥415  ≥22  ≤88  ≤183    Qualified

Welding Properties and Notice:
Low carbon and Nitrigon, Titanium and Niobium added, high corrosion-resisted performance on welding parts.
Difficult for Fusion wedding and etter for filler wire welding.
Low thermal expansion coefficient-high heat conduction and small deformation after welding comparing with 304.
Try to avoid heat imputing, otherwise result in bigger crystalline grain and influent the toughness of the plate.
Gas protection: Argon protection is needed to avoid surface oxidization and nitrizing.
To Avoid the contanmination of grease, otherwise carburization will occur.
Better to use 309L or higher grade welding rod.

Research and Development Target

400 series will be our research and developing target in future. Supper ferritic stainless steel will be hightlight, and as the substitute of 304 for our aim on the direction of economic research and developing. Realize 439 and 443 product seriation, enlarge the application of decorationg industry such ad the decoration of outside roof and curtain wall. Develop the high-chromium ferritic stainless steel such as 445, 446M and so on to improve the application of 400 series.

Service Promise
To provide consumers with the personalized designs on composition, propertiesproperty, packing, coil weight and quality certificate.
Technical support to customers in material selection fabrication.
Accurate and prompt delivery
Response to customer’s claim within 24 hours.

More technical details and the MTC require please visit our web site: www.gloriasteel.com  or contact us.

Contact Us
Alicia (Ms.) / Sales Manager

Tel:  +86-769-85325956
Fax: +86-769-82380569
Mob:+86-159-99718496
Email:Alicia@gloriasteel.com
MSN:Alicia-steel@hotmail.com
Skype:Alicia-steel
QQ:309801984