PP sheet is a semi -crystalline materials. It is more rigid than PE and has a higher melting point. Since the type of PP homopolymer 

temperature above 0 °C above is very brittle , so many commercial PP material is to add 1 to 4% ethylene random copolymer or a 

higher ratio of clamp-stage ethylene content copolymer. PP copolymer-based material has a lower heat distortion temperature (100 °C), low transparency, low gloss, low rigidity, but have a stronger impact strength. The strength of PP increases 

with increasing ethylene content . Vicat softening temperature of PP is 150 °C. Due to high crystallinity , surface of the material stiffness and good resistance to scratches . PP 

environmental stress cracking problem does not exist . Usually, the use of glass fiber , metal additives or

 thermoplastic rubber modified PP method . MFR PP turnover ranges from 1 to 40. Low MFR PP material better

 impact properties, but the extension of lower intensity . MFR for the same material , the intensity ratio of

 copolymer-based homopolymer to be higher . Because the crystal, PP contraction rate is very high, generally 1.8 to 2.5%.

 And the uniformity of the shrinkage direction than PE-HD material is much better . Adding 30 % glass additive can shrink rate fell to 0.7%. Homopolymer and 

copolymer PP materials have excellent resistance to moisture absorption , anti-acid corrosion and solvent resistance . However, it aromatic hydrocarbons ( such as benzene ) solvents,

 chlorinated hydrocarbons ( carbon tetrachloride ) solvents is not resistance. PP did not like PE at high 

temperatures still has antioxidant activity .