Hong Ye Jie Technology Co.,Ltd                                                                            

RTV-2 Silicone Rubber

RTV-2 room temperature addition silicone 

rubber

Model:  E630# 

Usage: Silicone rubber for mainly designed for 

metallic art & crafts and good grade mold 

making, pad printing etc.

 

Model	E-630#
Appearance	Yellowish Transparent
Mixing Ratio	1:1
Viscosity part A (Mpa.s)	23000±2000
Viscosity part B (Mpa.s)	2900±1000
Viscosity mixed(Mpa.s)	8000 ±2000
Operating time ( hrs 25℃)	0.5-2hrs
Curing time ( Hrs 25℃)	2~8hrs
Hardness (A°)	30±2
Tensile-strength(kgf /cm2 )	60±5
Tear-strength (Kgf/cm )	18±2
Elongation-break(%)	400±20
Retractility(%)	≤0.1

 

FEATURES:

 

★ Two-parts, flowable liquid silicone & curing agent.

Can solve the problem of not lighting of the candles and the problem of sticky and white stains on the surface of cement & stone products.

★ Good tensile strength and tear strength,low shrinkage.

★ It gets cured at room temperature 25 0C within 5-7 hours.

★ An exceptional fluidity and good operability, easy to be demolded.

★ Suitable for pouring methods of operation for small sized molds making.  

DESCRIPTION:

E630# addition molding silicone is generally named two-components silicone rubber, Part A and part B. It features an exceptional fluidity and good operability. The mixing ratio is 1:1,mainly be suitable for making molds application.

E630# addition cure silicone rubber is mainly used for molds making for food grade products. And it is also develop to solve the problem of not lighting of the candles and the problem of sticky and white stains on the surface of cement & stone products.

APPLICATIONS:

E630# addition molding silicone could be mainly used for making concrete stones, precision molds, PU molds, resin molds, gypsum casting, candle molding,for life casting, fabric finishing, seal for electronic components and solar circuit board, trademark decoration. etc.

OPERRATING INSTRUCTION: 

1.Stir part A and part B with right mixing ratio evenly. (E630# is 1:1) and get the mixture for vacuum-pumping.(If there is no vacuumizer,you can just pour the mixture slowly from the corner so that less bubbles caused).

2.Enclose the product (the original model) with four plastic plates or wooden plates.

3. Clean your products and brush a layer of release agent(detergent or soap water) on your product.

4.Pour the mixture with correct mixing ratio into the model frame. 

After about 2-4 hours, when the silicone cured, get out the original model, and there you get a finished addition cured silicone mold .

SHELF LIFE: 

Twelve (12) months from date of shipment when stored at 24℃ in original unopened packages.

PACKAGE:

Packed in clean 25kg/pail,  200kg/pail.

Pls kindly note:

Since this product is a newly develop one and is still on the path of promoting, We will offer you very competible price at this moment to suppport you on expanding the market and compete with other brands. This is a good chance for you to earn more money and occupy the market!

Sample is available for your testing. 

It is forbidden to mix with organic compounds of condensation cure silicone rubber, otherwise, the silicone rubber will not cure or valcanize. It also should keep from organic compounds containing S,P,N, and metal salt of organicacid which causing silicone not cure or unvulcanized.