Specifications
CAS NO: 9002-88-4
HS Code: 39012000
Apperance: granule&pellets
1, LLDPE film grade
Tests |
Value |
Unit |
Melt Flow Rate (MFR) |
2.0±0.4 |
g/10min |
Density |
920±2 |
Kg/cm3 |
Tensile Strengthat Yield |
8 |
Mpa ≥ |
Tensile Strengthat Break |
12 |
Mpa ≥ |
haze |
15 |
%≤ |
Packing |
In 25 kg PP woven bags,20MT/20’FCL |
2, LLDPE for Master Batch Use
Tests |
Value |
Unit |
Melt Flow Rate (MFR) |
20 |
g/10min |
Density |
0.924 |
g/cm3 |
Tensile Strength |
MD12 |
Mpa |
TD 10 |
||
Elongation at Yield |
13 |
% |
Elongation at Break |
200 |
|
Dark Drop Impact |
105 |
g |
Brittle Temperature(F 50) |
-70 |
°C |
Vicat Softening Point |
90 |
°C |
Packing |
In 25 kg PP woven bags,20MT/20’FCL |
3, LLDPE Powder Rotational Molding Grade for Tank Use
Tests |
Value |
Unit |
Melt Flow Rate (MFR) |
3.2 |
g/10min |
Density |
0.939 |
g/cm3 |
Melting Point |
127 |
°C |
Tensile Yield Strength |
21 |
Mpa |
Tensile Strength at Break |
28 |
Mpa |
Elongation at Break |
1,100 |
% |
Flexural Modulus |
750 |
Mpa |
Brittle Temperature |
<-60 |
°C |
Application
1 Fiber (Carpet, Textiles, Upholstery, etc.)
2 Film (Shopping bags, casting film, multilayer film, etc.)3 Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)4 Extrusion Molding (Sheet, Pipe, Wire & Cable, etc.)5 Injection Molding (Automotive, Electronic, Construction, House wares, Furniture,Toys, etc.)