Cast steel roll

Model:	-
Brand:	TINVO
Origin:	Made In China
Category:	Industrial Supplies / Machine Hardware / Capacitors
Label:	cast steel roll , mill rolls , rolling mill roll
Price:	-
Min. Order:	2 pc

Inquire Now

Product Description

Introduction

Alloy Cast Steel Roll is made of eutectoid steel and hypereutectoid steel. Alloy content greater than 0.8%, carbon content 0.4~1.3, Cr, Ni, Mo, V is added, matrix structure goes through heat treatment of normalizing and tempering, becoming sorbite and tempered sorbite.This type of mill roll has good strength, generally used for blooming and slab mills, section steel & bar wire rough rolling mill, etc. When the heat treatment system is the same, the wear resistance of cast steel roll is better than that of forging steel roll with the same composition, but the toughness is lower. Compare with forging steel roll, the cast steel roll is lower manufacturing cost.

Alloy steel rolls normally employ monoblock casting process (single pour): Melting-Casting-Heat treatment-Machining- Flaw detection- Finished products.

Chemical Composition

Alloy Material	C	Si	Mn	P	S	Ni	Cr	Mo
ZuS60SiCrNiMo	0.55~0.65	0.20~0.45	0.90~1.20	≤0.035	≤0.030		0.80~1.20	0.30~0.45
ZuS65SiCrNiMo	0.60~0.70	0.20~0.60	0.50~0.80	≤0.035	≤0.030	0.30~0.80	0.80~1.20	0.30~0.45
Zu70Mn	0.65~0.75	0.20~0.45	0.80~1.40	≤0.035	≤0.030
Zu70Mn2	0.65~0.75	0.20~0.45	1.40~1.80	≤0.035	≤0.030
Zu75CrMo	0.70~0.80	0.20~0.45	0.60~0.90	≤0.035	≤0.030		0.75~1.00	0.30~0.45
Zu75CrNiMnMo	0.70~0.80	0.20~0.60	0.60~1.10	≤0.035	≤0.030	0.30~1.00	0.90~1.20	0.30~0.45
Zu75Cr3NiMo	0.70~0.80	0.20~0.60	0.60~1.10	≤0.035	≤0.030	0.50~1.50	2.50~3.00	0.30~0.45
Zu80Cr	0.70~0.85	0.20~0.60	0.60~1.10	≤0.035	≤0.030	0.50~1.50	2.50~3.00	0.30~0.45

Physical Properties

Alloy Material	Roll-body hardness HSD	Tensile strength Mpa	Tension%	ToughnessJ/cm
ZuS60SiCrNiMo	32~42	≥740	≥5	≥8
ZuS65SiCrNiMo	35~45	≥800	≥5	≥8
Zu70Mn	35~45	≥740	≥5	≥8
Zu70Mn2	35~45	≥740	≥5	≥8
Zu75CrMo	36~46	≥770	≥5	≥8
Zu75CrNiMnMo	36~46	≥800	≥5	≥8
Zu75Cr3NiMo	45~55	≥700	≥3	≥5
Zu80Cr	38~48	≥790	≥5	≥7