Stainless Steel Welding Electrode E308L-16

Model:	E308L-16
Brand:	TEMO
Origin:	Made In China
Category:	Metallurgy , Mining & Energy / Metallurgy & Mining / Bars, Rods, Angles, and Stainless Steel Shapes
Label:	welding wire , welding electrode , welding rod
Price:	US $1500 / Ton
Min. Order:	0.2 Ton

Inquire Now

Product Description

Item NO.			GB/TB			AWS
WEA002			E308L-16			E308L-16
Description： Type of Cr19Ni10Mo ultra-low carbon stainless steel with coating of titanium calcium electrode.The carbon content in deposited metal less than or equal to 0.04％ with good intergranular corrosion satisfying.Both AC/DC connection applicable with excellent welding performance.
Application: WEA002 Stainless Steel Electrode apply to welding of stainless-steel of low carbon(Cr19Ni10).Can also be used to weld of corrosion resistance stainless steel under the operation temperature lower than 300℃.It is mainly used in synthetic fiber, fertilizer, petroleum equipment.
Chemical composition of Deposited metal(％):
C	Mn	Si	Cr	Ni	Mo	Cu	S	P
≤0.04	0.5-2.5	≤0.90	18.0-21.0	9.0-11.0	≤0.75	≤0.75	≤0.030	≤0.040
Mechanical Performance of deposited Metal:
Rm(Mpa)				A(％)
≥520				≥35
※The deposited metal corrosion resistance test and titanium content determined by supply and demand both sides negotiation.
Reference Current:(DC﹢or AC)
Diameter (mm)	Φ2.0		Φ2.5		Φ3.2		Φ4.0
Current (A)	25-50		50-80		80-110		110-160
Notes:(Ⅰ)Please bake WEA002 Stainless Steel Electrode for 1 hour at 150℃ before welding .(Ⅱ)We s est you to do the welding by DC and control the current to avoid redenning problem of rodes. By AC, the depth will not be enough.

right:.��slPM�cy border-left:none;width:108pt'>Φ4.0 Φ5.0 Current (A) 60-90 90-120 140-180 170-230 Notes:(Ⅰ)Please bake WE557 Low Alloy Steel Electrode for 1 hour at about 380℃ before welding .(Ⅱ)Clean the surface to be welded thoroughly to remove surface contaminations.(Ⅲ)Short arc must be used when welding and the weld joint shoulds not be too wide.