AISI h13 alloy hot tool steel flats   

1.Composition: 

C	Si	Mn	Cr	Mo	V	P	S
0.37-0.42	0.90-1.20	0.30-0.50	4.80-5.50	1.20-1.50	0.90-1.10	<0.03	<0.03

 

2. Equivalent Grades: 

GB	DIN	ASTM	JIS	BS	NF
4Cr5MoSiV1	1.2344	H13	SKD61	BH13	Z40CDV5

 

3. Size Available: 1) Round bar: Dia 16mm-600mm 

                              2) Flat bar: Thickness: 16-500mm Width: 200-1100mm 

                              Length can be customized.

 

4. Smelting Process: 1) EAF+LF+VD

                                    2) EAF+LF+VD+ESR

Note:EAF=Electric Arc Furnace; LF=Ladle Furnace; VD=Vacuum Degassing; ESR=Eleroslag Remelted.

  

5. Shaping: Hot forged / Hot rolled

 

6. Surface condition: Black surface/turning/milling/grinding/polishing

 

7. Annealing Hardness of tool steel blocks : HB230 Max

    Hardness after Q+T(quenching+tempering):47-49HRC

 

8. Hardness&tempering relationship:   aisi h13 alloy hot tool steel plate

 

 

9. Properties of H13:

Under medium temperature conditions, it has good toughness, thermal fatigue and wear resistance. High thermal strength and hardness. Less thermal deformation and less oxide skin when air quenching, erosion against molten aluminum. 

 

10. Application of  tool steel blocks :  aisi h13 alloy hot tool steel plate

Widely used in making hot extrusion die , core rod, pressing forging die, forging hammer die and precision forging die. And also used for the cooper and aluminum and alloy casting die .