Stress Control Heat Shrink Tubing For 36KV Terminations And Joints BH-SC360 

 

Applications:

BH-SC360 is made from radiation cross-linked polyolefin material,the specially designed

chemical formulation and carefully controlled manufacture technology makes the tube

effectively control the high electrical stress present at insulation termination of power

cables up to 36KV.

 

Features:

1) Shrink ratio: 2:1

2) Wall thickness: <3.0 mm

3)Voltage: up to 36KV

lectric stress relie

5) Made from radiation crosslinked polyolefin materials

6)  Effectively control high electrical stress at insulation screen in termination and joint of power cables 

7) Operating temperature :  -55℃~110℃

     Minimum shrink temperature: 100℃;

     Minimum fully recovery temperature: 130℃

8) Approvals / Specifications: RoHs

9) Standard color:  Black

 

Technical Data:

Property	Test Method	Typical Data
Tensile strength	ASTM D 638	≥10MPa
Elongation at break	ASTM D 638	≥300%
Heat Shock (200℃/30mins)	ESI09-13	No splitting, cracking dropping or flowing after 30 mins at 200℃
Dielectric constant	IEC 250	30~55
Volume Resistance	IEC 93	≥109Ω .cm
Low Temp Flexibility		No cracking after 4hrs at -20℃(max)
Water absorption	ISO 62	<1.0%
Longitudinal shrinkage	--	±5%
Eccentricity	ASTM S 2671	<35%

 

Product Dimensions (mm/inch):         

Normal size	As supplied (mm)	After recovered (mm)		Tube Shape	Standard Length(mm)
	Inside diameter(Min,)	Inside  diameter(Max.)	Wall  thickness(Min.)
Continuous length tubing
47/18	47	18	2.5	-	30M/Spool
Cut length tubing
55/21	55	21	2.5	o	1000-1220
65/25	65	25	2.5	o	1000-1220
75/30	75	30	2.5	o	1000-1220
95/45	95	45	3	o	1000-1220

 Tube Shape  “O”: round or oval, “-” : flattened shape.

 