OIL WELL CEMENTING FLUID LOSS ADDITIVE CG610S-T

 

 SUMMARY 

 

1. CG610S-T Fluid Loss Additive  can be used both for dry mixed and water mixed.

 

2. CG610S-T Fluid Loss Additive slurry system has wide applicable temperature range and it’s resistant

    to high temperature.

 

3. CG610S-T Fluid Loss Additive has salt resistance. It’s efficient in saturated brine.

 

4. CG610S-T Fluid Loss Additive slurry system is stable with little free fluid.  

 

5. CG610S-T Fluid Loss Additive slurry system is not retarded, fast strength development.

 

6. CG610S-T Fluid Loss Additive slurry system has excellent rheological behavior. It generally doesn’t 

    require adding dispersant.

 

 SPECIAL ATTENTIONS   

 

1. Fluid Loss Additive CG610S-T is easily caked after long storage. Although the performance of pro-

    duct is not affected, the product can not be dry-mixed for the loss of fluidity and become a little di-

    fficult to dissolve.

 

2. Fluid Loss Additive CG610S-T’s dosage should be increased if being used in brine or high tempera-

    ture system.

 

 APPLICATIONS 

 

 1.Temperature: Lower than 302°F (150°C) (BHCT) in fresh water system, lower than 356°F(180°C)

 (BHCT) in brine system.

   

2.Dosage: CG610S-T Fluid Loss Additive generally 1.6-4.0% (BWOC), recommended amount 1.8% 

(BWOC, in fresh water system, W/C=0.44).

 

CEMENT SLURRY PERFORMANCE 

 

 

Item				Technical Indicator
Initial consistency,Bc	80°C/45min, 46.5MPa			≤25
Thickening time,min				50~150
Fluid loss,ml	90°C, 6.9MPa			≤50
18% Brine fluid loss,ml	120°C, 6.9MPa			≤120
Free fluid,ml	90°C, Constant Pressure			≤3.5
24h Compressive strength,MPa				≥14
Composition:API class G(HSR) 700g;Fresh Water 308g;CG610S-T 12.6g(1.8%);
Composition:(18% brine system) API class G (HSR) 600g;silica flour 210g,18% brine 438g;CG610S-T 27g(4.5%);