Product Description

Forging Steel Ck 55 Description
CK55 steel has a higher (0.55%) carbon content for greater strength than the lower carbon alloys. It is hardenable by heat treatment, quench and tempering.

Designation by Standards

·        Brand Name: Ck 5

·        Mat No1.1203

·        DIN Ck55

·        EN -

·        AISI 1055

 

Chemical Composition

Chemical Composition

Properties

Metric

Imperial

Density

7.85 g/cc

0.284 lb/in3

 

APPLICATIONS

·        Steel for springs, for quenched and tempered springs, for surface hardened products like shafts, bushings, crankshafts, etc.

 

Physical Properties(average values) at ambient temperature

Show  entries

Search: 

Properties

Metric

Modulus of elasticity [10^3x N/mm2]

210

Density [lbs/in3]

7.85

Showing 1 to 2 of 2 entries

PreviousNext

 

Soft Annealing

·        Hardness after soft annealing 229 HB.

 

Hardening

·        Harden from a temperature of 840-870°C, 850-880°C followed by water or oil quenching.

 

Normalizing

·        Normalizing temperature (°C): 825-865°C.

 

Tempering

·        Tempering from the quenched condition may be done at 540 – 680°C depending upon the strength desired.

 

Mechanical Properties Vin Hardened+Tempered Condition

Diameter

0.2% proof stress

Tensile strength

Elongation A5

Reduction Z

(mm)

(Wmm 2 )

(Wmm2)

(%)

(%)

up to 16*

540

780-930

12

25

17-40

460

740-890

14

35

41-100

420

700-850

15

40

up to 16

430

630-780

17

40

 

Forging

·        Hot forming temperature: 1100-850°C.

 

Corrosion Resistance

·        This is a steel alloy and will rust if not protected. it is not corrosion resistant.

 

Welding

·        CK55 steel is weldable by all of the welding methods. However with its higher carbon content it is important to use both pre-heat at 150 to 260°C and post-heat at 590 to 650°C practice per an approved welding procedure.

 

Cold working

·        CompoIn the annealed state the CK55 alloy is readily cold worked by conventional methods.

 

 

Physical Properties

Quantity

Value

Unit

Thermal expansion

16 - 17

e-6/K

Thermal conductivity

16 - 16

W/m.K

Specific heat

500 - 500

J/kg.K

Melting temperature

1370 - 1400

°C

Service temperature

0 - 500

°C

Density

8000 - 8000

kg/m3

Resistivity

0.7 - 0.7

Ohm.mm2/m

THERMAL PROPERTIES

Properties

 

Conditions

 

 

 

T (°C)

Treatment

Thermal Conductivity (W/m-K)

42.7

100

 

Specific Heat (J/kg-K)

477

50-100
 

 

 

CK55/C55/1055 carbon steel bar 1

Member Information

Shandong Anniu Group
Country/Region:Shan Dong - China
Business Nature:Trading Company
Phone:92162059
Contact:Martin Ge (sales manager)
Last Online:02 Feb, 2015