Application：

calcined bauxite is typically calssified according to its intended commercial application,such as abrasive ,cement ,chemical, metallurgical, and refractory .as raw material for use in high alumina and super duty refratory bricks and shapes ,plastics ,castable refratory, motors, gun mixes, ramming mixes, abrasive grains and other products.

Calcined bauxite is widely used in:
1.aluminium metallurgy,
2 refractory material,
3 precision casting,
4 aluminate cement

1.Shaft kiln bauxite
Al2o3: 80-85% min.
Fe2o3: 1.5-2.0% max.

B.D.: 3.10g/cm-3.25g/cm min.

2. Downdraft kiln bauxite

Al2o3: 80-90% min.
Fe2o3: 1.5-2.0% max.
B.D.: 3.10g/cm-3.35g/cm min.

3.Rotary kiln bauxite
Al2o3: 80-90% min.
Fe2o3: 1.5-2.0% max.
B.D.: 3.10g/cm-3.35g/cm min.