| Specifications: |
|
Bore Diameter
|
Wall Thickness
|
|
Nominal (mm)
|
Tolerance （±）
|
Minimum
|
Maximum
|
|
0.5,0.8
|
±0.10
|
0.20
|
0.50
|
|
1.0,1.5
|
±0.20
|
0.20
|
0.60
|
|
2.0,2.5,3.0
|
±0.20
|
0.20
|
0.70
|
|
3.5,4.0,5.0,6.0
|
±0.25
|
0.30
|
0.70
|
|
7.0,8.0
|
±0.25
|
0.30
|
1.00
|
|
9.0,10.0
|
±0.50
|
0.40
|
1.00
|
|
12.0
|
±0.50
|
0.40
|
1.20
|
|
14.0,16.0,18.0,20.0,23.0
|
±1.00
|
0.40
|
1.20
|
|
25.0,27.0,30.0
|
±1.00
|
0.40
|
1.40
|
|
| Advantages: |
|
Performance
|
Requirements
|
|
Breakdo wn Voltage（KV）
|
Median
|
Median
|
Minimum value
|
|
under normal（23±2℃）
|
≥4.0
|
≥2.5
|
|
High temperature（155±2℃）
|
≥2.0
|
≥1.5
|
|
Moist heat treatment
|
≥1.5
|
≥1.2
|
|
Resistance to soldering heat
|
To maintain the temperature of the solder at 260 ° C ± 5 ° C, the middle of the hose vertical section of the lower end of 6mm immersed in the molten solder bath, tinned copper maintained in the molten solder bath 15s ± 1s. Hose shall not crack or obvious swelling.
|
|
Bending resistance after heating
|
Temperature: 180 ° C ± 3 ° C, processing time 48h ± 1h, hose wrapped around the mandrel, the film should not be disengaged or cracking the glass tube.
|
|
Bending low temperatures
|
Temperature: ≤ -35 ℃± 2 ° C, the processing time of 240min ± 10min, the outside of the paint film should glass tube disengaged or cracking.
|
|
Spread of flame resistance
|
≤60S
|
|
Temperature index
|
200℃
|
|