Fine Si3N4 bonded SiC  Thermocouple Sheath is a sort of structure ceramic material, NSiC product is shaped by casting with the composition of high pure SiC and Si powder, and sintered through nitrified reaction.

 

NSiC has higher strength than RSiC and has excellent oxidation resistance. Maximum working temperature is 1500deg.In addition to its structural properties, NSiC has excellent wear properties and is resistant to corrosion and erosion by molten metals. So that it can be used in direct contact with molten aluminum, zinc, copper, magnesium. NSiC has been successfully used for Thermocouple Sheath for temperature measurement.

 

Thermocouple Sheath offer many engineering property levels that are not found in other refractory materials, such as high strength at using temperature, excellent load bearing strength and resistance to chemical and abrasive attack.

 

 

 

Characteristic:

 

1.    Excellent oxidation resistance

 

2.    Good wear resistance

 

3.    Excellent corrosion resistance

 

4.    High temperature flexural performance

 

5.    Excellent load bearing strength

 

 

 

The Data Sheet Of The NSiC

 

Bulk Density: 2.75-2.82g/cm3

 

Porosity: 10-12%

 

Compression Strength: 600-700Mpa

 

Bending Strength: 160-180Mpa

 

Young’s Modulus: 220-260Gpa

 

Thermal Conductivity: 15W/MK

 

Thermal Expansion α（20-1000℃）: 5.0x10-6k-1

 

Max. Working Temperature: 1500℃

 

Si3N4: 20-40%

 

SiC: 60-80%